Monitoring Stress Corrosion Cracking in Sensitized 304 Stainless Steel Using Acoustic Emission, Corrosion Potential, and Visualization of Fe²⁺ Dissolution

アコースティック・エミッション法,腐食電位計測およびFe²⁺の溶解反応の可視化法を用いた鋭敏化されたオーステナイト系ステンレス鋼SUS304の応力腐食割れの計測

Author (2)： CHO Hideo (Aoyama Gakuin Univ., Kanagawa, JPN) ,  NISHIMIYA Kojiro (Aoyama Gakuin Univ., Kanagawa, JPN)
Material： 日本海水学会誌  (Bulletin of the Society of Sea Water Science, Japan)
Volume： 73  Issue： 6  Page： 347-351  Publication year： Dec. 01, 2019 
JST Material Number： F0235A  ISSN： 0369-4550  CODEN： NKAGBU  Document type： Article
Article type： 短報  Country of issue： Japan (JPN)  Language： ENGLISH (EN)

Thesaurus term： *austenitic stainless steel ,  *stress corrosion cracking ,  stress corrosion ,  corrosion mechanism ,  flaw inspection ,  acoustic emission ,  corrosion potential ,  metal ion ,  iron compound ,  visualization ,  crack propagation ,  iron ion ,  *crack ,  *corrosion cracking ,  mechanism

JST classification (2)： Corrosion  (WB03030B) ,  Materials for chemical equipment  (XB01020D)

Reference (7)：

• 1)J. Kovac, M. Leban and A. Legat, Detection of SCC on prestressing steel wire by the simultaneous use of electrochemical noise and acoustic emission measurements, Electrochimica Acta, 52, 7607-7616(2007)
• 2)B. Cox, A correlation between acoustic emission during SCC and fractography of cracking of the zircaloys, Corrosion, 30, 191-202(1974)
• 3)D.G. Chakrapani and E.N. Pugh, The transgranular SCC of a Mg-Al alloy: Crystallographic, fractographic and acoustic-emission studies, Metallurgical Transaction A, 6A, 1155-1163(1975)
• 4)S. Fujimoto, M. Takemoto and K. Ono, Acoustic emission monitoring of chloride stress corrosion cracking of austenitic stainless steel, J. Acoustic Emission, 19, 63-72(2001)
• 5)H. Inoue, Electrochemical Noise Analysis for Predicting the Initiation of Localized Corrosion, Bull.Soc.Sea Water Sci. Jpn., 61, 159-161(2007)

Terms in the title (9)： アコースティック・エミッション ,  腐食電位 ,  計測 ,  Fe2+ ,  溶解 ,  可視化 ,  オーステナイト系ステンレス鋼 ,  SUS304 ,  応力腐食割れ