Evaluation of Machinability on Solid-Solution Strengthened Ferritic Ductile Iron

固溶強化した球状黒鉛鋳鉄の切削性評価

Author (3)： HATTORI SUGURU (三重県工研) ,  MURAKAWA SATORU (三重県工研) ,  HIO KATSUYA (三重県工研)
Material： 三重県工業研究所研究報告  (Reports of the Mie Prefecture Industrial Research Institute)
Issue： 43  Page： 27-32  Publication year： Dec. 25, 2019 
JST Material Number： Z0229B  ISSN： 2185-016X  Document type： Article
Article type： 原著論文  Country of issue： Japan (JPN)  Language： JAPANESE (JA)

Thesaurus term： *nodular graphite cast iron ,  graphite spheroidizing ,  *cutting ability ,  elongation ,  matrix(base) ,  ferrite structure ,  solid solution ,  pearlite ,  surface quality ,  cutting force ,  tool wear ,  tensile strength ,  *solid solution hardening ,  silicon containing alloy

JST classification (1)： Various techniques for casting  (WC01040B)

Reference (7)：

• Wolfram Stets et al.: “Solution strengthened ferritic ductile cast iron according DIN EN 1563: 2012- properties, production and application”. 2013 Keith Millis Symposium on Ductile Cast Iron, p283-292 (2013)
• Richard Larker: “Solution strengthened ferritic ductile iron ISO 1083/JS/500-10 provides superior consistent properties in hydraulic rotators”. China Foundry, 6(4), p343-351 (2009)
• 梅谷拓郎ほか:“高Siフェライト基地球状黒鉛鋳鉄の引張強さ,疲労強度,衝撃強さ”. 鋳造工学,86(1),p36-42 (2014)
• 尾上豪浩ほか:“高けい素球状黒鉛鋳鉄の機械的性質・組織に及ぼすマンガン・ニッケルの影響”.三重県工業研究所研究報告,42,p15-19 (2018)
• 堀江 皓ほか:“新版 鋳鉄の生産技術”.(財) 素形材センター,p29-42 (2012)

Terms in the title (3)： 球状黒鉛鋳鉄 ,  切削性 ,  評価