Superconducting Joint for REBCO-Coated Conductors without Oxidization Annealing via Low-temperature Synthesis Reaction Using Potassium Hydroxide

水酸化カリウムによる低温合成反応を利用した 酸素アニール処理不要なREBCO 線材の超電導接合

Author (4)： FUNAKI SHUHEI (島根大学大学院自然科学研究科) ,  MIYACHI YUGO (島根大学大学院自然科学研究科) ,  MIYACHI YUGO (日本学術振興会(特別研究員DC)) ,  YAMADA YASUJI (島根大学大学院自然科学研究科)
Material： 低温工学  (Journal of Cryogenics and Superconductivity Society of Japan)
Volume： 55  Issue： 4  Page： 275-279(J-STAGE)  Publication year： 2020 
JST Material Number： S0846A  ISSN： 0389-2441  Document type： Article
Article type： 原著論文  Country of issue： Japan (JPN)  Language： JAPANESE (JA)

Thesaurus term： *potassium hydroxide ,  *chemical synthesis ,  Oxygen ,  annealing (heat treatment) ,  *barium compound ,  *rare earth element compound ,  *metal oxide ,  *copper compound ,  superconducting wire ,  *superconducting junction ,  mechanical press ,  transition temperature ,  X-Ray Diffraction ,  *Low temperature synthesis ,  *Rare-earth barium copper oxide ,  superconducting transition temperature
Semi thesaurus term： anneal treatment ,  *REBCO ,  superconducting wire ,  superconducting critical temperature ,  XRD analysis

Author keywords (4)： superconducting joint ,  REBCO ,  low temperature ,  KOH

JST classification (1)： Superconducting materials  (BM04041W)

Reference (23)：

• 1) L. Goodrich and J. Ekin: “Lap joint resistance and intrinsic critical current measurements on a NbTi superconducting wire,” IEEE Trans. Magn. 17 (1981) 69-72
• 2) Y.J. Park, M.W. Lee, Y.K. Oh and H.G. Lee: “Laser drilling: enhancing superconducting joint of GdBa₂Cu₃O_{7-δ coated conductors,” Supercond. Sci. Technol. 27 (2014) 085008}
• 3) K. Ohki, T. Nagaishi, T. Kato, D. Yokoe, T. Hirayama, Y. Ikuhara, T. Ueno, K. Yamagishi, T. Takao, R. Piao, H. Maeda and Y. Yanagisawa: “Fabrication, microstructure and persistent current measurement of an intermediate grown superconducting (iGS) joint between REBCO-coated conductors,” Supercond. Sci. Technol. 30 (2017) 115017
• 4) K. Hiramatsu, R. Teranishi, K. Yamada, Y. Sato and K. Kaneko: “Joint of REBa₂Cu₃O7-_δ coated conductors using metal organic deposition,” Phys. Procedia 81 (2016) 109-112
• 5) T. Miyajima, R. Teranishi, S. Yasuyama, Y. Sato, K. Kaneko, T. Maeda, M. Ochi, K. Hiramatsu, M. Nakamura, V. Petrykin, S. Lee, T. Okada and S. Awaji: “Microstructures of superconducting joint between GdBa₂Cu₃O_7-y-coated conductors via additionally deposited precursor films,” Jpn. J. Appl. Phys. 58 (2019) 020913

Terms in the title (7)： 水酸化カリウム ,  低温合成 ,  酸素 ,  アニール処理 ,  REBCO ,  線材 ,  超電導接合