AL-ZN-IN合金の微細構造と電気化学的性質に及ぼすERの影響を研究した。【JST・京大機械翻訳】

Effect of Er on Microstructure and Electrochemical Performance of Al-Zn-In Anode

著者 (7件)： Li Hang (Key Laboratory of Nonferrous Materials and New Processing Technology, Guangxi University) ,  Wei Bing (Key Laboratory of Nonferrous Materials and New Processing Technology, Guangxi University) ,  Xu Zhengbing (Key Laboratory of Nonferrous Materials and New Processing Technology, Guangxi University) ,  Zeng Jianmin (Key Laboratory of Nonferrous Materials and New Processing Technology, Guangxi University) ,  Chen Rong (Key Laboratory of Nonferrous Materials and New Processing Technology, Guangxi University) ,  Li Heng (Key Laboratory of Nonferrous Materials and New Processing Technology, Guangxi University) ,  Lu Yanyan (Key Laboratory of Nonferrous Materials and New Processing Technology, Guangxi University)
資料名： Xiyou Jinshu Cailiao yu Gongcheng  (Xiyou Jinshu Cailiao yu Gongcheng)
巻： 45  号： 7  ページ： 1848-1854  発行年： 2016年 
JST資料番号： W0563A  ISSN： 1002-185X  CODEN： XJCGEA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： AL-ZN-INアノード合金の微細構造に及ぼすER含有量の影響を,SEM,EDS,およびXRDによって研究した。3.5%(質量分率)NACL溶液中で異なるER含有量のAL-5ZN-0.03IN-ER合金の分極曲線と電気化学インピーダンス(EIS)を測定した。結果は以下を示す。ER含有量の増加とともに,アルミニウム合金アノードの樹枝状晶は微細化し,樹枝状晶間の析出相は増加し,合金の腐食電位は正にシフトし,EISスペクトルの半径は増加し,腐食速度は減少した。4種類の合金の中で、AL-5ZN-0.03IN-1ER合金の樹枝状結晶はある程度の細粒化、析出物の中に存在し、食は比較的に独立で、均一な腐食の特徴を呈し、陽極合金材料とすることができる。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 樹枝状結晶 ,  *微細構造 ,  腐食速度 ,  精密化 ,  粉化 ,  電気化学インピーダンス ,  腐食電位 ,  X線回折 ,  析出物 ,  アルミニウム合金 ,  *合金 ,  スペクトル
準シソーラス用語： 分極曲線 ,  質量分率 ,  *電気化学的特性 , 【Automatic Indexing@JST】

著者キーワード (5件)： Al-Zn-In sacrificial alloy ,  Er ,  microstructure ,  polarization curve ,  EIS

分類 (3件)： 変態組織,加工組織  (WB01030N) ,  鋳造欠陥  (WC01060X) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (4件)： 微細構造 ,  電気化学的性質 ,  Er ,  研究