C/C-SIC複合材料の構造と特性に及ぼす素密度の影響を研究した。【JST・京大機械翻訳】

Effects of Preform Density on Structure and Property of C/C-SiC Composites Fabricated by Gaseous Silicon Infiltration

著者 (6件)： Cao Yu (College of Aerospace and Materials Engineering, National University of Defense Technology) ,  Liu Rongjun (College of Aerospace and Materials Engineering, National University of Defense Technology) ,  Cao Yingbin (College of Aerospace and Materials Engineering, National University of Defense Technology) ,  Long Xianhai (College of Aerospace and Materials Engineering, National University of Defense Technology) ,  Yan Chunlei (College of Aerospace and Materials Engineering, National University of Defense Technology) ,  Zhang Changrui (College of Aerospace and Materials Engineering, National University of Defense Technology)
資料名： Cailiao Gongcheng  (Cailiao Gongcheng)
巻： 44  号： 7  ページ： 19-25  発行年： 2016年 
JST資料番号： C2125A  ISSN： 1001-4381  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 化学的気相浸透(CVI VAPOR INFILTRATION,CVI)により,三次元針刺TanZhanを調製した。C/C-SIC複合材料を,気相ケイ(GSI SILICON INFILTRATION,GSI)により調製した。C/C-SIC複合材料の機械的性質と熱的性質に及ぼす素密度の影響を研究した。結果は以下を示す。素密度が増加するにつれて、CVI C層が厚くなり、多孔度が減少した。C/C-SIC複合材料中の残留C量は増加し,残留SI量は減少し,そして,SIC含有量は,最初に増加し,次に減少し,そして,C/C-SIC複合材料の密度は,徐々に減少し,そして,機械的性質は,最初に増加し,次に減少した。しかし,熱伝導率と熱膨張係数は定常状態に低下した。密度が1.085G/CM3のとき,複合材料の機械的性質は最良であり,曲げ強さは308.31MPAに達し,破壊靭性は11.36MPA M(1/2)であった。素の多孔性が大きい場合には,ケイのチャネルは十分で,残留シリコンは多く,CVI C層は薄く,繊維層は硅Shi,C/C-SIC複合材料の機械的性質は低い。素の多孔性が小さい場合、ケイチャネルが速く閉塞し、SIとSICの含有量が少なく、閉鎖孔が大きく、しかもC/C-SIC複合材料の力学性能も高くない。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 曲げ強さ ,  三次元 ,  熱伝導率 ,  *複合材料 ,  破壊靱性 ,  機械的性質 ,  熱膨張係数 ,  気相 ,  多孔性 ,  熱特性 ,  浸透 ,  チャネル ,  空隙率
準シソーラス用語： 機械的性能 ,  定常状態 , 【Automatic Indexing@JST】

著者キーワード (5件)： C/C preform ,  GSI ,  C/C-SiC composite ,  CVI C ,  mechanical property