活性スクリーンプラズマイオン浸炭,3CR13ステンレス鋼の組織と性能に及ぼす温度の影響を窒化【JST・京大機械翻訳】

Effect of Nitrocarburizing Temperature on Microstructure and Properties of Active Screen Plasma Nitrocarburizing Layer of 3Cr13 Stainless Steel

著者 (5件)： Zhang Lingling (Department of Materials, Kunming University of Science and Technology, Guangdong Provincial Key Laboratory of Modern Surface Engineering Technology) ,  Hou Huijun (Guangdong Provincial Key Laboratory of Modern Surface Engineering Technology, New Materials Department, Guangdong General Research Institute of Non-ferrous Metals) ,  Zhan Zhaolin (Department of Materials, Kunming University of Science and Technology) ,  Wei Chunbei (Guangdong Provincial Key Laboratory of Modern Surface Engineering Technology, New Materials Department, Guangdong General Research Institute of Non-ferrous Metals) ,  Kong Weihuan (Department of Materials, Kunming University of Science and Technology, Guangdong Provincial Key Laboratory of Modern Surface Engineering Technology)
資料名： Rejiagong Gongyi  (Rejiagong Gongyi)
巻： 45  号： 4  ページ： 113-116  発行年： 2016年 
JST資料番号： C2487A  ISSN： 1001-3814  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： イオン活性スクリーンプラズマ浸炭窒化を共浸透技術を採用し,そして光学顕微鏡とX線回折で儀対Shen層の組織形態と成分を採用し,分析を行い,3CR13ステンレス鋼に対し,異なる温度の下で処理を行った。微小硬さ、ボール-ディスク摩擦摩耗試験、走査電子顕微鏡によって材料の硬さ及び摩擦摩耗特性を検討した。その結果,処理温度の上昇とともに,試料の表層の相組成から’+Α_N相+Ε相Γ’’相は徐々にΑ相+CRN相+Ε相に変換する,試料表面の増加は微小硬さは,摩耗率は約1桁低下したが,耐摩耗性は向上する。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 摩耗特性 ,  耐摩耗性 ,  摩耗試験 ,  *窒化 ,  表層 ,  走査電子顕微鏡 ,  浸炭窒化 ,  相組成 ,  微小硬さ ,  *イオン浸炭 ,  硬度 ,  浸透 ,  摩耗率 ,  円板 ,  *ステンレス鋼

著者キーワード (5件)： 3Cr13 stainless steel ,  active screen plasma nitrocarburizing ,  temperature ,  microstructure ,  wear resistance

分類 (4件)： 固体の機械的性質一般  (BL01021C) ,  表面硬化熱処理  (WC03030E) ,  気相めっき  (WC08022K) ,  金属の機械的性質  (BL01022T)

タイトルに関連する用語 (7件)： 活性 ,  スクリーン ,  プラズマ ,  イオン浸炭 ,  ステンレス鋼 ,  組織 ,  窒化