Wを添加した熱処理中のTi46Al6Nb-(Si,B)合金のミクロ組織の発達【Powered by NICT】

Microstructure evolution of Ti-46Al-6Nb-(Si,B) alloys during heat treatment with W addition

著者 (8件)： Cao Shouzhen (School of Materials Science and Engineering, Harbin Institute of Technology) ,  Xiao Shulong (School of Materials Science and Engineering, Harbin Institute of Technology) ,  Chen Yuyong (School of Materials Science and Engineering, Harbin Institute of Technology) ,  Tian Jing (School of Materials Science and Engineering, Harbin Institute of Technology) ,  Xu Lijuan (School of Materials Science and Engineering, Harbin Institute of Technology) ,  Wang Xiaopeng (School of Materials Science and Engineering, Harbin Institute of Technology) ,  Han Jianchao (School of Materials Science and Engineering, Harbin Institute of Technology) ,  Jia Yi (School of Materials Science and Engineering, Harbin Institute of Technology)
資料名： Rare Metals  (Rare Metals)
巻： 35  号： 1  ページ： 85-92  発行年： 2016年 
JST資料番号： C2573A  ISSN： 1001-0521  CODEN： RARME8  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： Ti46Al6Nb-0.25Si-0.2BとTi46Al6Nb-5Cr-0.25Si-0.2B(at%)の鋳造インゴットを誘導加熱スカル融解(ISM)法によって作製した。一連の熱処理(HT)の両合金のミクロ組織変化を研究するために実施した。走査電子顕微鏡(SEM),X線回折(XRD),透過型電子顕微鏡(TEM),および引張試験機で調べたミクロ組織と引張特性。結果はミクロ偏析(液体偏析と固体偏析)は0.5Wの添加により悪化することを示した;TiAl合金中のNb,Wの添加は困難に起こる相転移を起こす,両合金のミクロ組織と引張性質をあるHTプロセス後改善される最後に,HTプロセス後γ/α_2ラメラの厚さは炉冷モーメント前の残留C相の数に大きく影響された。Data from the ScienceChina, LCAS.【Powered by NICT】

シソーラス用語： 徐冷 ,  鋳造 ,  走査電子顕微鏡 ,  インゴット ,  X線回折 ,  *熱処理 ,  偏析 ,  誘導加熱 ,  引張 ,  透過型電子顕微鏡 ,  *合金 ,  引張特性 ,  微細構造進展 ,  チタンアルミ合金
準シソーラス用語： チタンアルミニウム合金 ,  ミクロ偏析 , 【Automatic Indexing@JST】

著者キーワード (5件)： TiAl合金 ,  熱処理 ,  W添加 ,  微細構造進化 ,  ミクロ偏析