冷間圧延およびアニーリング後の15Mn O1C-0 4/1.4Al Si TRIP/TWIP鋼の相組成【Powered by NICT】

Phase composition of 15Mn-0.1C-0.4/1.4Al-Si TRIP/TWIP steels after cold rolling and annealing

著者 (7件)： Podany Pavel (Department of Materials Analysis, COMTES FHT Inc., Dobrany, Czech Republic) ,  Dlouhy Jaromir (Department of Materials Analysis, COMTES FHT Inc., Dobrany, Czech Republic) ,  Koukolikova Martina (Department of Materials Analysis, COMTES FHT Inc., Dobrany, Czech Republic) ,  Martinek Petr (Department of Materials Analysis, COMTES FHT Inc., Dobrany, Czech Republic) ,  Prochazka Radek (Department of Materials Analysis, COMTES FHT Inc., Dobrany, Czech Republic) ,  Kubina Tomas (Department of Materials Analysis, COMTES FHT Inc., Dobrany, Czech Republic) ,  Duchek Michal (Department of Materials Analysis, COMTES FHT Inc., Dobrany, Czech Republic)
資料名： IEEE Conference Proceedings  (IEEE Conference Proceedings)
巻： 2016  号： ICMAE  ページ： 121-126  発行年： 2016年 
JST資料番号： W2441A  資料種別： 会議録 (C)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 鉄鋼業では,研究努力は主に最近高強度鋼に焦点を当てた。これらの鋼は,自動車産業と(構造部品の重量減少のおかげで)航空機産業において使用されている。今世紀の初めに出現した新しい可能性,γ相の歪誘起変態の影響をオーステナイト鋼に適用することを試みた。特に高マンガン鋼は変形核形成双晶の発生に起因する加工硬化率の高さにより特性化し,おそらくマルテンサイトの変形誘起生成と組み合わせて,極めて延性オーステナイト鋼である。エネルギー吸収の能力を,通常の鋼と比較してはるかに大きかった。本論文では,厚さが40%減少した冷間圧延後のアニーリング後のマンガンの15wt.%の二熱鋼の相組成の記述を検討した。相解析の種々の方法を用いた:カラーエッチング,EBSDとX線回折した。Copyright 2016 The Institute of Electrical and Electronics Engineers, Inc. All Rights reserved. Translated from English into Japanese by JST【Powered by NICT】

シソーラス用語： マンガン ,  自動車工業 ,  マルテンサイト ,  加工誘起変態 ,  *相組成 ,  双晶 ,  重量損失 ,  *冷間圧延 ,  延性 ,  オーステナイト鋼 ,  X線回折 ,  *焼なまし ,  エネルギー吸収 ,  キャラクタリゼーション ,  *鋼

分類 (3件)： 図形・画像処理一般  (JE04010I) ,  信号理論  (ND02020G) ,  分子・遺伝情報処理  (JE15040B)

タイトルに関連する用語 (6件)： 冷間圧延 ,  アニーリング ,  Si ,  TRIP ,  TWIP鋼 ,  相組成