Hot tearing susceptibility of Mg-xZn-2Y alloys

著者 (7件)： Wang Zhi (School of Materials Science and Engineering, Shenyang University of Technology) ,  Li Yizhou (School of Materials Science and Engineering, Shenyang University of Technology) ,  Wang Feng (School of Materials Science and Engineering, Shenyang University of Technology) ,  Huang Yuanding (MagIC-Magnesium Innovation Centre, Helmholtz-Zentrum Geesthacht) ,  Song Jiangfeng (MagIC-Magnesium Innovation Centre, Helmholtz-Zentrum Geesthacht) ,  Mao Pingli (School of Materials Science and Engineering, Shenyang University of Technology) ,  Liu Zheng (School of Materials Science and Engineering, Shenyang University of Technology)
資料名： Transactions of Nonferrous Metals Society of China  (Transactions of Nonferrous Metals Society of China)
巻： 26  号： 12  ページ： 3115-3122  発行年： 2016年 
JST資料番号： W0396A  ISSN： 1003-6326  CODEN： TNMCEW  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： MG-2%Y合金の耐食性に及ぼすZN含有量(0,0.5%,1.5%および4.5%)の影響を,力センサおよびデータ収集システムを用いて研究した。実験結果は,ZN元素を添加しない合金が最も低い傾向を持つことを示した。ZN含有量が増加するにつれて,MG-2%Y合金の耐食性は増加し,ZN含有量が1.5%のときに最大値に達し,次にZN含有量の増加とともに熱裂敏感傾向が低下した。凝固過程において,MG-1.5ZN-2Y合金は,より大きい収縮力と凝固収縮力のために,合金化の傾向が最も大きい。MG-XZN-2Y系合金の熱的亀裂は,樹枝状晶または結晶粒界に沿って発生した。PROCASTソフトウェアによるシミュレーション結果は,実験結果と一致した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： ソフトウェア ,  亀裂 ,  *合金 ,  シミュレーション ,  データ収集システム ,  樹枝状結晶 ,  *相溶性 ,  凝固 ,  結晶粒界 ,  耐食性 ,  合金化
準シソーラス用語： 力センサ , 【Automatic Indexing@JST】

著者キーワード (4件)： Mg-xZn-2Y alloy ,  hot tearing susceptibility ,  solidification contraction force ,  numerical simulation