酸化膜構成の変遷と走査型プローブ顕微鏡によるナノスケールで推定した臨界応力【Powered by NICT】

Transition of oxide film configuration and the critical stress inferred by scanning probe microscopy at nanoscale

著者 (9件)： Fang Xufei (AML, Department of Engineering Mechanics, Tsinghua University, Beijing 100084, China) ,  Fang Xufei (Center for Mechanics and Materials, Tsinghua University, Beijing 100084, China) ,  Li Yan (AML, Department of Engineering Mechanics, Tsinghua University, Beijing 100084, China) ,  Li Yan (Center for Mechanics and Materials, Tsinghua University, Beijing 100084, China) ,  Zhang Changxing (AML, Department of Engineering Mechanics, Tsinghua University, Beijing 100084, China) ,  Zhang Changxing (Center for Mechanics and Materials, Tsinghua University, Beijing 100084, China) ,  Dong Xuelin (Key Laboratory of Petroleum Engineering, China University of Petroleum, Beijing 102249, China) ,  Feng Xue (AML, Department of Engineering Mechanics, Tsinghua University, Beijing 100084, China) ,  Feng Xue (Center for Mechanics and Materials, Tsinghua University, Beijing 100084, China)
資料名： Chemical Physics Letters  (Chemical Physics Letters)
巻： 660  ページ： 33-36  発行年： 2016年 
JST資料番号： B0824A  ISSN： 0009-2614  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 高温ナノインデンテーション装置に装備された走査型プローブ顕微鏡(SPM)はナノスケールでのNi基単結晶上の酸化物膜成長を特性化in situで採用されている。SPM画像は本来平坦な表面は,酸化中に粗くする酸化物膜配置の転移を明らかにした。酸化中の応力-拡散結合効果に基づいて,酸化物膜における応力進展と表面形態の発展を解析した。転移点における酸化物膜における臨界応力を推定する新しい方法をSPMで得られた表面形態に基づく波形表面波長を測定することにより提案した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 高温 ,  画像 ,  *走査型プローブ顕微鏡 ,  転移温度 ,  ナノインデンテーション ,  *酸化 ,  表面波 ,  単結晶 ,  拡散接合 ,  キャラクタリゼーション ,  *酸化膜
準シソーラス用語： 表面形態 ,  *臨界応力 ,  *ナノスケール , 【Automatic Indexing@JST】

著者キーワード (5件)： 走査型プローブ顕微鏡法 ,  酸化物膜 ,  ストレス ,  ナノスケール ,  表面

分類 (1件)： 原子・分子のクラスタ  (BH09030O)

タイトルに関連する用語 (5件)： 酸化膜 ,  走査型プローブ顕微鏡 ,  ナノスケール ,  推定 ,  臨界応力