紙の強化性能に及ぼす新しい高分子ネットワークの影響を研究した。【JST・京大機械翻訳】

Influence of new interpenetrating polymer networks on the paper strengthing properties

著者 (5件)： Liu Yan (Key Laboratory of Auxiliary Chemistry & Technology for Chemical Industry,Ministry of Education, Shaanxi University of Science and Technology) ,  Shen Yiding (Key Laboratory of Auxiliary Chemistry & Technology for Chemical Industry,Ministry of Education, Shaanxi University of Science and Technology) ,  Fei Guiqiang (Key Laboratory of Auxiliary Chemistry & Technology for Chemical Industry,Ministry of Education, Shaanxi University of Science and Technology) ,  Wang Haihua (Key Laboratory of Auxiliary Chemistry & Technology for Chemical Industry,Ministry of Education, Shaanxi University of Science and Technology) ,  Fan Dan (Key Laboratory of Auxiliary Chemistry & Technology for Chemical Industry,Ministry of Education, Shaanxi University of Science and Technology)
資料名： Gongneng Cailiao  (Gongneng Cailiao)
巻： 47  号： 9  ページ： 9132-9137  発行年： 2016年 
JST資料番号： C2095A  ISSN： 1001-9731  CODEN： GOCAEA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： アクリルアミド(AM),メタクリル酸グリシジル(GMA),メタクリル酸グリシジル(DMC)を,反応媒体としてポリアミドアミン(PAE)溶液を用いて,過硫酸アンモニウムを開始剤として使用した。ラジカル重合の方法を用いて,イオン型型型相互貫入ネットワーク重合体(IPN)を調製した。赤外スペクトルは,ラジカル重合が成功したことを示した。SEMの結果は,異なる比率のPAEとCPAMの混合物が,空間ネットワーク架橋構造を持つことを示した。研究により、Ω(PAE)=60.56、Ω(AM)=2.42%、Ω(DMC)=2.42%、重合温度70°C、時間3Hの条件下で、固形分30%の陽イオン相互貫入ネットワークポリマーを紙に応用した。IPNの添加量が1%のとき,紙指数は17.44,向上指数は26.78,裂傷指数は39.84,耐は%,耐性指数は41.49%であった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 重合開始剤 ,  *ネットワーク ,  ラジカル重合 ,  媒質 ,  赤外スペクトル ,  カチオン ,  *高分子
準シソーラス用語： 固形分 ,  重合温度 ,  架橋構造 ,  ペルオキソ二硫酸アンモニウム , 【Automatic Indexing@JST】

著者キーワード (6件)： PAE ,  AM ,  DMC ,  free radical polymerization ,  interpenetrating polymer networks ,  strengthing properties

分類 (1件)： 共重合  (CG04030D)

タイトルに関連する用語 (4件)： 紙 ,  強化 ,  高分子ネットワーク ,  研究