生物医学的応用の可能性を持つNiフリーZr基バルク金属ガラスのトライボロジー挙動【Powered by NICT】

Tribological behavior of a Ni-free Zr-based bulk metallic glass with potential for biomedical applications

著者 (18件)： Hua Nengbin (Department of Materials Science and Engineering, Fujian University of Technology, 350118 Fuzhou, China) ,  Hua Nengbin (Department of Materials Science and Engineering, Fuzhou University, 350116 Fuzhou, China) ,  Hua Nengbin (Fujian Provincial Key Laboratory of Advanced Materials Processing and Application, 350118 Fuzhou, China) ,  Chen Wenzhe (Department of Materials Science and Engineering, Fujian University of Technology, 350118 Fuzhou, China) ,  Chen Wenzhe (Department of Materials Science and Engineering, Fuzhou University, 350116 Fuzhou, China) ,  Chen Wenzhe (Fujian Provincial Key Laboratory of Advanced Materials Processing and Application, 350118 Fuzhou, China) ,  Wang Weiguo (Department of Materials Science and Engineering, Fujian University of Technology, 350118 Fuzhou, China) ,  Wang Weiguo (Fujian Provincial Key Laboratory of Advanced Materials Processing and Application, 350118 Fuzhou, China) ,  Lu Haotian (Department of Materials Science and Engineering, Fujian University of Technology, 350118 Fuzhou, China) ,  Lu Haotian (Fujian Provincial Key Laboratory of Advanced Materials Processing and Application, 350118 Fuzhou, China) ,  Ye Xiaoyun (Department of Materials Science and Engineering, Fujian University of Technology, 350118 Fuzhou, China) ,  Ye Xiaoyun (Fujian Provincial Key Laboratory of Advanced Materials Processing and Application, 350118 Fuzhou, China) ,  Li Guanghui (Department of Materials Science and Engineering, Fujian University of Technology, 350118 Fuzhou, China) ,  Li Guanghui (Fujian Provincial Key Laboratory of Advanced Materials Processing and Application, 350118 Fuzhou, China) ,  Lin Chen (Department of Materials Science and Engineering, Fujian University of Technology, 350118 Fuzhou, China) ,  Lin Chen (Fujian Provincial Key Laboratory of Advanced Materials Processing and Application, 350118 Fuzhou, China) ,  Huang Xufang (Department of Materials Science and Engineering, Fujian University of Technology, 350118 Fuzhou, China) ,  Huang Xufang (Fujian Provincial Key Laboratory of Advanced Materials Processing and Application, 350118 Fuzhou, China)
資料名： Materials Science & Engineering. C. Materials for Biological Applications  (Materials Science & Engineering. C. Materials for Biological Applications)
巻： 66  ページ： 268-277  発行年： 2016年 
JST資料番号： W0574A  ISSN： 0928-4931  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,Niを含まないZr_53Al_16Co_2325Ag_7 0.75バルク金属ガラス(BMG)のトライボロジー挙動をボールオンディスク往復摩擦を用いた乾燥滑りと模擬生理的媒体中で研究した。のZr-Al-CO-Ag BMGの耐摩耗性に及ぼす滑り荷重,速度,媒体と相手材料の影響を図示した。空気中での乾燥滑りの下で,Zr基BMGの耐摩耗性は滑り負荷と共に減少し,摩耗劣化は酸化とアブレシブ摩耗によって制御される。滑り速度を増加させると,より大きな塑性変形が摩擦熱に起因するBMGの表面で起こる。BMGは0.9%NaClで減少した摩耗抵抗と空気と脱イオン水の場合と比較してリン酸緩衝食塩水(PBS)溶液,研磨磨耗や腐食摩耗の相乗効果により制御されたトライボ腐食と関連しているを示した。Si_3N_4相手材に対するZr基BMGの耐摩耗性はZrO_2に対するそれより劣るが,症例であるAl_2O_3に対するものとは反対であった。BMGの耐摩耗性に及ぼすセラミック相手材料の影響を,それらのYoung率および破壊靭性に基づいて議論した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 破壊靱性 ,  塩水 ,  アブレシブ摩耗 ,  塩化ナトリウム ,  滑り速度 ,  脱イオン水 ,  耐摩耗性 ,  *ジルコニウム ,  塑性変形 ,  *ニッケル ,  Young率 ,  摩耗 ,  *バルク金属ガラス ,  相乗作用
準シソーラス用語： 乾燥滑り , 【Automatic Indexing@JST】

著者キーワード (5件)： バルク金属ガラス ,  ジルコニウム合金 ,  トライボロジー挙動 ,  乾燥滑り ,  腐食摩耗

分類 (1件)： 医用素材  (GA05040H)

タイトルに関連する用語 (6件)： 生物医学的応用 ,  可能性 ,  Niフリー ,  Zr ,  バルク金属ガラス ,  トライボロジー挙動