マイクロアロイド鋼板における変形誘起フェライト変態による表面層の結晶粒微細化【Powered by NICT】

Grain refinement in surface layers through deformation-induced ferrite transformation in microalloyed steel plate

著者 (6件)： Shen X.J. (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, China) ,  Tang S. (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, China) ,  Chen J. (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, China) ,  Liu Z.Y. (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, China) ,  Misra R.D.K. (Department of Metallurgical, Materials and Biomedical Engineering, University of Texas at El Paso, 500 W. University Avenue, El Paso, TX 79968, USA) ,  Wang G.D. (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, China)
資料名： Materials & Design  (Materials & Design)
巻： 113  ページ： 137-141  発行年： 2017年 
JST資料番号： A0495B  ISSN： 0264-1275  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 新しい熱機械的プロセスを採用してマイクロアロイド鋼板の表面層における変形誘起超微細粒フェライトを得ることであった。圧延結合水冷制御プロセスと呼ぶ新しいプロセスは圧延中水冷を適用した。変形誘起フェライト変態は板の表面層における超微細フェライト結晶粒(1 3μm)をもたらした,板の全厚さの約13.5%に超微細結晶粒層を考慮した。厚さでは,比較的粗大フェライト粒(7.8μm)とパーライト微細構造が得られた。超微細結晶粒構造に対応する延性-脆性遷移温度は 118°Cであり,完全な板の平均衝撃靭性が高いことをそのような表面層で得られた優れた靭性。表面での超微細結晶粒構造の形成の機構を明らかにした。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 超微粒子 ,  靱性 ,  *結晶粒 ,  延性 ,  *フェライト ,  微結晶 ,  *表層 ,  圧延 ,  パーライト ,  *結晶粒微細化 ,  水冷 ,  *マイクロアロイド鋼
準シソーラス用語： 衝撃靱性 ,  脆性遷移温度 ,  *フェライト変態 , 【Automatic Indexing@JST】

著者キーワード (5件)： マイクロアロイド鋼板 ,  靱性 ,  圧延結合水冷制御プロセス ,  変形誘起フェライト変態 ,  超微細フェライト

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (5件)： マイクロアロイド鋼 ,  誘起 ,  フェライト変態 ,  表面層 ,  結晶粒微細化