PU/PUポリウレタンフォーム複合材料の調製と難燃性を研究した。【JST・京大機械翻訳】

Preparation and Flame Retardant Properties of Ceramic Polyurethane Foam Composite

著者 (6件)： Chen Fei (State Key Lab of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology) ,  Sun Wanwan (State Key Lab of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology) ,  Jiang Jinglu (Hubei Xinhuaguang Information Materials Co Ltd) ,  Hu Sheng (State Key Lab of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology) ,  Shen Qiang (State Key Lab of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology) ,  Zhang Lianmeng (State Key Lab of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology)
資料名： Wuhan Ligong Daxue Xuebao  (Wuhan Ligong Daxue Xuebao)
巻： 38  号： 4  ページ： 1-7  発行年： 2016年 
JST資料番号： W0729A  ISSN： 1671-4431  CODEN： WLDXAV  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 難燃剤として白雲母(MICA),ポリリン酸アンモニウム(APP),および膨張性黒鉛(EG)を用いて,一段階水熱起泡法により,ポリウレタンフォーム複合材料を調製した。走査電子顕微鏡,X線回折,熱重量分析,および限界酸素指数(LOI)を用いて,生成物の微細構造,相,熱分解プロセス,および難燃性を特性評価した。結果は,MICA/APP/EG/PU複合材料が,可瓷化/PU複合材料の高温アブレーション後の多孔性セラミック相構造を形成することができることを示して,それは,可瓷化/PU複合材料を首尾よく調製することができた。セラミック_4,KAL_3SI_3O_(11)およびKAL_5O_8の主成分は,発泡の含有量が20%,APP含量が8%,EG含量が2%であった。PU/MICA/APP/EGの800°Cでの残留率はポリウレタン(PU)よりも299%%高く,複合材料は高温耐性だけでなく高温残留率も高く,PU/MICA/APP/EGのLOI値は34.5%に達し,難燃性は優れていることを示した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *難燃性 ,  高温 ,  走査電子顕微鏡 ,  難燃剤 ,  X線回折 ,  熱分解 ,  起泡 ,  *複合材料 ,  多孔性 ,  熱重量分析 ,  キャラクタリゼーション
準シソーラス用語： LOI【酸素】 ,  *ポリウレタンフォーム ,  膨張黒鉛 ,  ポリリン酸アンモニウム , 【Automatic Indexing@JST】

著者キーワード (4件)： mica ,  ceramic polyurethane foam ,  thermal degradation ,  flame retardant properties

分類 (1件)： 難燃剤  (YH05060Q)

タイトルに関連する用語 (6件)： Pu ,  ポリウレタンフォーム ,  複合材料 ,  調製 ,  難燃性 ,  研究