熱伝導率,高分子繊維強化高体積パーム油燃料灰を混合したモルタルの圧縮と残留強度評価【Powered by NICT】

Thermal conductivity, compressive and residual strength evaluation of polymer fibre-reinforced high volume palm oil fuel ash blended mortar

著者 (5件)： Mo Kim Hung (Department of Civil Engineering, Faculty of Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia) ,  Bong Chun Siung (Department of Civil Engineering, Faculty of Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia) ,  Alengaram U. Johnson (Department of Civil Engineering, Faculty of Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia) ,  Jumaat Mohd Zamin (Department of Civil Engineering, Faculty of Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia) ,  Yap Soon Poh (Department of Civil Engineering, Faculty of Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 130  ページ： 113-121  発行年： 2017年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 高分子繊維強化高体積パーム油燃料灰(POFA)混合モルタルの特性の研究を報告した。非構造建築材料のための目標とする用途を考慮して,熱伝導率,圧縮と残留強度だけでなく,モルタルの水吸収を評価した。0.3vol.%を超えるPOFAと高分子繊維(ポリプロピレンとアクリル)の導入は,一般的に熱伝導率と圧縮強度が減少するとともに,モルタルの水吸収を増加させた。POFAの混入により,高温に曝露した強度損失を減少させなかったが,0.3%以上の繊維の添加は,圧縮強度損失の低減にわずかな影響を持っていた。,熱伝導率,圧縮強度と残留強度の観点から最適化に基づいて,建築材料中の非構造応用のための0.3vol.%を超える高分子繊維の高い体積POFA及び添加が有用と推奨した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *モルタル ,  高温 ,  *熱伝導率 ,  *残留強度 ,  最適化 ,  *パーム油 ,  建築材料 ,  圧縮強さ
準シソーラス用語： *高分子繊維 , 【Automatic Indexing@JST】

著者キーワード (4件)： 熱伝導率 ,  残留強度 ,  高分子繊維 ,  パーム油燃料灰

分類 (1件)： モルタル,コンクリート  (RA06042H)

タイトルに関連する用語 (10件)： 熱伝導率 ,  高分子繊維 ,  強化 ,  体積 ,  パーム油 ,  燃料 ,  灰 ,  モルタル ,  残留強度 ,  評価