液滴堆積法により調製した多孔性フレキシブルグラフェン導電膜【JST・京大機械翻訳】

Preparation of graphene transparent flexible conductive film via liquid surface deposition

著者 (8件)： Yuan Chunqiu (Nanjing University of Posts And Telecommunications, Institute of Advanced Materials (IAM)) ,  Zeng Wenjin (Nanjing University of Posts And Telecommunications, Institute of Advanced Materials (IAM)) ,  Tang Wei (Nanjing University of Posts And Telecommunications, Institute of Advanced Materials (IAM)) ,  Zhao Chunyan (Nanjing University of Posts And Telecommunications, Institute of Advanced Materials (IAM)) ,  Mo Shenbin (Nanjing University of Posts And Telecommunications, Institute of Advanced Materials (IAM)) ,  Wang Jian (Nanjing University of Posts And Telecommunications, Institute of Advanced Materials (IAM)) ,  Yu Youhai (Xi’an Institute of Optics and Precision Mechanics of Chinese Academy of Science) ,  Min Yonggang (Nanjing University of Posts And Telecommunications, Institute of Advanced Materials (IAM))
資料名： Gongneng Cailiao  (Gongneng Cailiao)
巻： 47  号： 9  ページ： 9143-9148  発行年： 2016年 
JST資料番号： C2095A  ISSN： 1001-9731  CODEN： GOCAEA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 透明導電性膜は,現代の電子分野で広く使用されている。簡単な液面堆積法を用いてフレキシブル基板上にPET基板上に酸化グラフェン薄膜を成功裏に調製し,室温でヨウ(HI)蒸気還元によりグラフェン透明導電膜を得た。異なる堆積層数のグラフェン薄膜の透過率と導電性との関係を,SEM,TEM,AFM,吸収スペクトル(UV-VIS),および電気抵抗分析(法)を用いて研究した。グラフェン蒸着層数の増加により導電膜の導電性は上昇したが,薄膜の透過率は低下した。透過率(Λ=550NM)が82.22のとき,導電性膜のシート抵抗は620Ω/□であった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： フレキシブル基板 ,  透明導電膜 ,  *多孔性 ,  吸収スペクトル ,  薄膜 ,  蒸着 ,  透過率 ,  シート抵抗 ,  *グラフェン ,  *液滴 ,  導電性
準シソーラス用語： 堆積層 ,  酸化グラフェン ,  *導電膜 , 【Automatic Indexing@JST】

著者キーワード (3件)： graphene ,  liquid deposition ,  flexible transmittance conductive thin films

分類 (2件)： 炭素とその化合物  (YB02060D) ,  その他の無機化合物の薄膜  (BK14060A)

タイトルに関連する用語 (6件)： 液滴 ,  堆積 ,  調製 ,  多孔性 ,  グラフェン ,  導電膜