均質化ボーキサイト原料と速度論的研究の一段階焼結【Powered by NICT】

One step sintering of homogenized bauxite raw material and kinetic study

著者 (6件)： Gao Changhe (School of Material Science and Engineering, University of Science and Technology Beijing) ,  Jiang Peng (School of Material Science and Engineering, University of Science and Technology Beijing) ,  Li Yong (School of Material Science and Engineering, University of Science and Technology Beijing) ,  Sun Jialin (School of Material Science and Engineering, University of Science and Technology Beijing) ,  Zhang Junjie (Gongyi Tongda Zhongyuan Refractory Technology Co., Ltd.) ,  Yang Huanying (School of Material Science and Engineering, University of Science and Technology Beijing)
資料名： International Journal of Minerals, Metallurgy and Materials  (International Journal of Minerals, Metallurgy and Materials)
巻： 23  号： 10  ページ： 1231-1238  発行年： 2016年 
JST資料番号： W1051A  ISSN： 1674-4799  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： 直接採掘からボーキサイト原料の一段階焼結工程が完了した,このプロセスの動力学を十分に解析した。結果は,ボーキサイト原料の焼結速度は液相焼結挙動を示すことが分かった。原料中に存在する不純物の小部分は液相として作用した。X線回折分析,走査電子顕微鏡観察,および速度論計算後,焼結温度および加熱時間は,ボーキサイト鉱石の焼結過程と緻密化に寄与する二つの主要な因子として決定した。高い加熱温度とより長い継続時間は緻密化プロセスを促進した。ボーキサイト材料の緻密化のための主要な障害は,液相焼結中の囲まれたブローホールの形成に起因する。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： 緻密化 ,  不純物 ,  *ボーキサイト ,  加熱温度 ,  液相 ,  *速度論 ,  継続時間 ,  X線回折分析 ,  *焼結 ,  液相焼結 ,  *均質化
準シソーラス用語： 加熱時間 ,  焼結温度 ,  走査電子顕微鏡法 ,  焼結速度 , 【Automatic Indexing@JST】

著者キーワード (4件)： ボーキサイト ,  耐火材料 ,  液相焼結 ,  焼結速度論的研究