複合材料の機械的性質に及ぼすカーボンナノチューブ含有量の影響を研究した。【JST・京大機械翻訳】

Effect of the Content of Carbon Nanotubes on the Mechanical Properties of Aluminum Matrix Composites

著者 (5件)： Liu Qiang (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University) ,  Ke Liming (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University; National Defence Key Discipline Laboratory of Light Alloy Processing Science and Technology) ,  Huang Chunping (National Defence Key Discipline Laboratory of Light Alloy Processing Science and Technology, Nanchang Hangkong University) ,  Liu Fencheng (National Defence Key Discipline Laboratory of Light Alloy Processing Science and Technology, Nanchang Hangkong University) ,  Mao Yuqing (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University)
資料名： Cailiao Daobao  (Cailiao Daobao)
巻： 30  号： 10B  ページ： 67-70  発行年： 2016年 
JST資料番号： C2126A  ISSN： 1005-023X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 多層カーボンナノチューブ強化アルミニウム基(/)複合材料を,摩擦撹拌加工によって調製し,そして,複合材料の機械的性質に及ぼすカーボンナノチューブ含有量の影響を研究した。結果は,MWCNTSの添加が,複合材料の機械的性質に著しい影響を及ぼし,MWC-NTSの含有量が増加するにつれて,複合材料の硬度,弾性率,および強度が増加することを示した。カーボンナノチューブの含有量は6であった。6%(体積分率)のとき,複合材料の強度は218MPAに達し,マトリックス材料の2であった。24倍;MWCNTS含有量の増加とともに,//複合複合材料の塑性は,徐々に悪くなり,そして,引張伸びは,徐々に減少し,そして,破壊ディンプルは,徐々に小さくなり,そして,薄くなった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 伸び ,  *機械的性質 ,  弾性係数 ,  *カーボンナノチューブ ,  体積率 ,  摩擦撹拌処理 ,  塑性 ,  *複合材料 ,  硬度
準シソーラス用語： ディンプル , 【Automatic Indexing@JST】

著者キーワード (3件)： friction stir processing ,  multi-walled carbon nanotubes content ,  mechanical properties