ナノ準結晶Al-Fe-Cr-Ti合金マトリックス/γAl_2O_3ナノ複合材料粉末のボールミル処理の影響【Powered by NICT】

Nanoquasicrystalline Al-Fe-Cr-Ti alloy matrix/γ-Al₂O₃ nanocomposite powders: The effect of the ball milling process

著者 (5件)： Xu W. (Department of Materials, University of Oxford, 16 Parks Road, OX1 3PH, Oxford, United Kingdom) ,  Galano M. (Department of Materials, University of Oxford, 16 Parks Road, OX1 3PH, Oxford, United Kingdom) ,  Audebert F. (Department of Materials, University of Oxford, 16 Parks Road, OX1 3PH, Oxford, United Kingdom) ,  Audebert F. (Advanced Materials Group, INTECIN (UBA-CONICET), Facultad de Ingenieria, Universidad de Buenos Aires, Paseo Colon 850, Ciudad de Buenos Aires, 1063, Argentina) ,  Audebert F. (Department of Mechanical Engineering and Mathematical Sciences, Oxford Brookes University, Wheatley Campus, OX33 1HX, Oxford, United Kingdom)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 701  ページ： 342-349  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 市販アルミニウム合金上での高強度の利点を持つ準結晶アルミニウム合金とアルミニウム基ナノ複合材料は長年研究されている。本研究ではナノ準結晶Al-Fe-Cr-Ti合金粉末とナノ準結晶合金とナノサイズγAl_2O_3粉末の混合物から成るナノ複合材料を,異なるミリング速度で機械的ミリングによって作製した。より高いミル処理時間あるいはミル処理速度はγAl_2O_3分布の均一性を向上させることができることが観察された。α-Al結晶粒径は減少し,硬さはミリング時間と共に増加した。最小結晶サイズ(14 nm)と最高の硬度値(638HV_10g)は250rpmで30時間粉砕後のナノ複合材料が得られた。α-Al結晶粒径はボールミリングプロセス中のミクロ組織における主要な変化であるので,粉砕した粉末の硬さの変化は 0.25の指数を持つHall-Petchタイプの関係に従うことが分かった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *準結晶 ,  *合金 ,  結晶粒径 ,  *アルミニウム ,  *粉体 ,  アルミニウム合金 ,  硬度 ,  *ナノ複合材料 ,  加工時間 ,  *結晶 ,  合金粉
準シソーラス用語： 処理速度 ,  高強度 ,  *ボールミル摩砕 , 【Automatic Indexing@JST】

著者キーワード (5件)： メカニカルミリング ,  アルミニウム ,  準結晶 ,  Nanocomposites ,  Hardness