ポリアクリル酸/酸化グラフェン自己修復ヒドロゲルの合成と性能【JST・京大機械翻訳】

Preparation and Performance of Poly (acrylic acid)/Graphene Oxide Self-healing Hydrogels

著者 (5件)： Li Haiyan (Provincial Key Laboratory of Oil Gas Chemical Technology, College of Chemistry&Chemical Engineering, Northeast Petroleum University) ,  Li Shuang (Provincial Key Laboratory of Oil Gas Chemical Technology, College of Chemistry&Chemical Engineering, Northeast Petroleum University) ,  Wang Qi (Provincial Key Laboratory of Oil Gas Chemical Technology, College of Chemistry&Chemical Engineering, Northeast Petroleum University) ,  Cui Yexiang (Provincial Key Laboratory of Oil Gas Chemical Technology, College of Chemistry&Chemical Engineering, Northeast Petroleum University) ,  Ma Yingjie (Provincial Key Laboratory of Oil Gas Chemical Technology, College of Chemistry&Chemical Engineering, Northeast Petroleum University)
資料名： Zhongguo Suliao  (Zhongguo Suliao)
巻： 30  号： 11  ページ： 42-47  発行年： 2016年 
JST資料番号： C2259A  ISSN： 1001-9278  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 酸化グラフェン(GO)を,改良HUMMERS法により首尾よく調製した。ポリアクリル酸(PAA)/GO自己修復ヒドロゲルを,架橋剤としてFE(3+),架橋剤としてアクリル酸(AA)を用いて,IN SITU重合によって調製した。異なるの自己修復ヒドロゲルの膨潤特性を,異なるGO含有量の下で研究し,そして,自己修復ヒドロゲルの機械的性質に及ぼすGO含有量,FE(3+)含有量およびH_2O含有量の影響を研究し,そして,自己修復ヒドロゲルの自己修復性能を研究した。その結果,FE(3+)含量,GO含量及びH_2O含有量はそれぞれ0.5%(モル分率)及び0.5%(質量分率),80%であることが判明した。最適機械的性質(引張強さは743.5KPA,破断伸びは2940.5%%)であった。GO含有量が0.25%のとき,PAA/GOの自己修復ヒドロゲルの吸水性は最大値に達した。PAA/GO自己修復ヒドロゲルは優れた自己修復性を有していた。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 引張強さ ,  重合 ,  モル分率 ,  膨潤 ,  *ヒドロゲル ,  機械的性質
準シソーラス用語： 吸水性 ,  破断伸び ,  質量分率 ,  自己修復性 ,  *自己修復 , 【Automatic Indexing@JST】

著者キーワード (5件)： hydrogel ,  graphene oxide ,  poly(acrylic acid) ,  self-healing ,  mechanical property

分類 (2件)： 炭素とその化合物  (YB02060D) ,  充填剤,補強材  (YH05030J)

タイトルに関連する用語 (4件)： ポリアクリル酸 ,  酸化グラフェン ,  自己修復 ,  ヒドロゲル