効率的なナノ構造化太陽電池を達成するための2段階アルカリエッチング法による前組織化多結晶シリコンウエハ【Powered by NICT】

Pre-texturing multi-crystalline silicon wafer via a two-step alkali etching method to achieve efficient nanostructured solar cells

著者 (14件)： Hu Fenqin (College of Physics, Optoelectronics and Energy, Collaborative Innovation Center of Suzhou Nano-Science and Technology, Soochow University, 1 Shizi Street, Suzhou 215006, China) ,  Hu Fenqin (Jiangsu Key Laboratory of Thin Films, Soochow University, 1 Shizi Street, Suzhou 215006, China) ,  Sun Yun (College of Physics, Optoelectronics and Energy, Collaborative Innovation Center of Suzhou Nano-Science and Technology, Soochow University, 1 Shizi Street, Suzhou 215006, China) ,  Sun Yun (Jiangsu Key Laboratory of Thin Films, Soochow University, 1 Shizi Street, Suzhou 215006, China) ,  Zha Jiawei (College of Physics, Optoelectronics and Energy, Collaborative Innovation Center of Suzhou Nano-Science and Technology, Soochow University, 1 Shizi Street, Suzhou 215006, China) ,  Zha Jiawei (Jiangsu Key Laboratory of Thin Films, Soochow University, 1 Shizi Street, Suzhou 215006, China) ,  Chen Kexun (College of Physics, Optoelectronics and Energy, Collaborative Innovation Center of Suzhou Nano-Science and Technology, Soochow University, 1 Shizi Street, Suzhou 215006, China) ,  Chen Kexun (Jiangsu Key Laboratory of Thin Films, Soochow University, 1 Shizi Street, Suzhou 215006, China) ,  Zou Shuai (College of Physics, Optoelectronics and Energy, Collaborative Innovation Center of Suzhou Nano-Science and Technology, Soochow University, 1 Shizi Street, Suzhou 215006, China) ,  Zou Shuai (Jiangsu Key Laboratory of Thin Films, Soochow University, 1 Shizi Street, Suzhou 215006, China) ,  Fang Liang (College of Physics, Optoelectronics and Energy, Collaborative Innovation Center of Suzhou Nano-Science and Technology, Soochow University, 1 Shizi Street, Suzhou 215006, China) ,  Fang Liang (Jiangsu Key Laboratory of Thin Films, Soochow University, 1 Shizi Street, Suzhou 215006, China) ,  Su Xiaodong (College of Physics, Optoelectronics and Energy, Collaborative Innovation Center of Suzhou Nano-Science and Technology, Soochow University, 1 Shizi Street, Suzhou 215006, China) ,  Su Xiaodong (Jiangsu Key Laboratory of Thin Films, Soochow University, 1 Shizi Street, Suzhou 215006, China)
資料名： Solar Energy Materials and Solar Cells  (Solar Energy Materials and Solar Cells)
巻： 159  ページ： 121-127  発行年： 2017年 
JST資料番号： D0513C  ISSN： 0927-0248  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： アルカリ溶液は,異方性エッチングによるテキスチャード加工多結晶シリコン(mc Si)ウエハには適していない。本研究では,二段階アルカリエッチプロセスは,ウエハ,水酸化ナトリウム溶液,続いて水酸化ナトリウム次亜塩素酸ナトリウム溶液による浸漬によりエッチングされた等方的に迅速かつほぼに平坦な表面を形成するために開発した。エッチングプロセスは均一なナノ構造の形成をもたらし,それによって短絡電流と開回路電圧が同時に増加することによって細胞の再現性と性能を改善した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 浸漬 ,  *ポリシリコン ,  *ナノ構造 ,  短絡電流 ,  水酸化ナトリウム ,  *太陽電池 ,  *多結晶 ,  再現性 ,  テキスチャード加工
準シソーラス用語： 開回路電圧 ,  次亜塩素酸ナトリウム ,  異方性エッチング ,  アルカリ溶液 ,  *シリコンウエハ , 【Automatic Indexing@JST】

著者キーワード (5件)： 多結晶シリコン太陽電池 ,  2段階アルカリエッチング ,  金属触媒化学エッチング ,  ナノtexture ,  電力変換効率

分類 (1件)： 太陽電池  (NC03084O)

タイトルに関連する用語 (7件)： ナノ構造 ,  太陽電池 ,  段階 ,  アルカリエッチング ,  組織化 ,  多結晶シリコン ,  ウエハ