BN ZrO_2~-SiC複合材料の低温焼結挙動と機械的性質【Powered by NICT】

Low-temperature sintering behavior and mechanical properties of BN-ZrO₂-SiC composites

著者 (5件)： Chen Lei (Institute for Advanced Ceramics, Harbin Institute of Technology, Harbin 150001, China) ,  Wang Yujin (Institute for Advanced Ceramics, Harbin Institute of Technology, Harbin 150001, China) ,  Ouyang Jia-Hu (Institute for Advanced Ceramics, Harbin Institute of Technology, Harbin 150001, China) ,  Duan Xiaoming (Institute for Advanced Ceramics, Harbin Institute of Technology, Harbin 150001, China) ,  Zhou Yu (Institute for Advanced Ceramics, Harbin Institute of Technology, Harbin 150001, China)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 681  ページ： 50-55  発行年： 2017年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 比較的低い焼結温度で高密度BN ZrO_2~-SiC複合材を作製するために使用されてきた新しい圧力支援過渡粘性相焼結プロセス。過渡粘性相としてB_2O_3を組み込んだBN ZrO_2~-SiC複合材料の焼結挙動と緻密化機構を調べた。迅速ち密化プロセスは約1300°Cで起こり,それはZrO_2,SiCとB_2O_3間の化学反応によるSiO_2のその場形成に起因した。100MPa下で1300°Cで焼結したBN ZrO_2~-SiC複合材料は相対密度95.9%,242MPaの曲げ強さと4.1MPa√m~1/2の破壊靭性を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 緻密化 ,  *複合材料 ,  破壊靱性 ,  化学反応 ,  粘性 ,  相対密度 ,  機械的性質 ,  *焼結 ,  *炭化ケイ素 ,  曲げ強さ
準シソーラス用語： 高密度 ,  焼結温度 ,  *低温焼結 , 【Automatic Indexing@JST】

著者キーワード (4件)： BN ZrO_2~-SiC複合材料 ,  過渡粘性焼結 ,  ち密化機構 ,  機械的性質