Mg_66Zn_30Gd_4合金の非晶質メルトスパンリボンの電気抵抗率と結晶化挙動の温度依存性【Powered by NICT】

Temperature dependence of resistivity and crystallization behaviors of amorphous melt-spun ribbon of Mg₆₆Zn₃₀Gd₄ alloy

著者 (5件)： Zhang Jinyang (School of Materials Science and Engineering, University of Jinan, No. 336, West Road of Nan Xinzhuang, Jinan 250022, PR China) ,  Teng Xinying (School of Materials Science and Engineering, University of Jinan, No. 336, West Road of Nan Xinzhuang, Jinan 250022, PR China) ,  Xu Shumin (School of Materials Science and Engineering, University of Jinan, No. 336, West Road of Nan Xinzhuang, Jinan 250022, PR China) ,  Ge Xingjing (School of Materials Science and Engineering, University of Jinan, No. 336, West Road of Nan Xinzhuang, Jinan 250022, PR China) ,  Leng Jinfeng (School of Materials Science and Engineering, University of Jinan, No. 336, West Road of Nan Xinzhuang, Jinan 250022, PR China)
資料名： Materials Letters  (Materials Letters)
巻： 189  ページ： 17-20  発行年： 2017年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本論文では,Mg基Mg_66Zn_30Gd_4非晶質リボンを単ロール溶融紡糸法を用いて作製することに成功した。合金リボンの非等温結晶化挙動を示差走査熱量測定(DSC)と比抵抗法で調べ,その結晶化過程とミクロ構造をX線回折,透過型電子顕微鏡(TEM)および制限視野電子回折(SAED)により確認した。結果は抵抗率(TCR)の負の温度係数は結晶化プロセスに存在し,溶融紡糸Mg_66Zn_30Gd_4リボンの結晶化過程は三段階から構成されていることを示した。約385Kでの最初の結晶化反応はICQ相の生成とそれに続くMg_7Zn_3二元相とMg_3(Gd, Zn)三元相(468 538K)の形成により,約538Kでα-Mg相の形成に関係している。ICQ相の形成は二十面体局所秩序の遺伝を反映している。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *温度依存性 ,  二十面体 ,  示差走査熱量測定 ,  *非晶質 ,  透過型電子顕微鏡 ,  非晶質リボン ,  *結晶化 ,  *電気抵抗率 ,  制限視野回折 ,  溶融紡糸 ,  *合金 ,  X線回折
準シソーラス用語： NTC【係数】 ,  非等温結晶化 ,  *結晶化挙動 , 【Automatic Indexing@JST】

著者キーワード (4件)： 非晶質材料 ,  電気的性質 ,  マグネシウム合金 ,  結晶化挙動

分類 (2件)： 非晶質金属の構造  (BK04020D) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (6件)： 非晶質 ,  メルトスパン ,  リボン ,  電気抵抗率 ,  結晶化挙動 ,  温度依存性