押出し自由成形によるYBa_2Cu_3O_7x(YBCO)超伝導体バルク構造の作製【Powered by NICT】

Fabrication of YBa₂Cu₃O_7-x (YBCO) superconductor bulk structures by extrusion freeforming

著者 (6件)： Wei Xiangxia (Department of Materials Science and Engineering, National University of Singapore, 117574, Singapore) ,  Nagarajan Ragavendran Sundaram (Department of Materials Science and Engineering, National University of Singapore, 117574, Singapore) ,  Peng Erwin (Department of Materials Science and Engineering, National University of Singapore, 117574, Singapore) ,  Xue Junmin (Department of Materials Science and Engineering, National University of Singapore, 117574, Singapore) ,  Wang John (Department of Materials Science and Engineering, National University of Singapore, 117574, Singapore) ,  Ding Jun (Department of Materials Science and Engineering, National University of Singapore, 117574, Singapore)
資料名： Ceramics International  (Ceramics International)
巻： 42  号： 14  ページ： 15836-15842  発行年： 2016年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 高温超伝導体の実用化は,複雑な形状に加工であることを必要とするかもしれない。本研究では,高温処理と結合したスラリー系押出自由成形はバルクYBa_2Cu_3O_7x(YBCO)超伝導構造の作製を試みた。理論密度の約93%をもつYBCO部分は940°Cで60時間焼結後に作製した,得られた構成相熱処理温度と時間に強く依存することに成功した。高臨界転移温度(T=92K)と良好な磁気浮上能力は熱処理条件の最適化後に得られた。全体として,実験結果は,押出自由成形は,望ましい配置と良好な超伝導特性を有することをYBCO超伝導体を作製するための実行可能で有効な技術であることを実証した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 臨界 ,  高温超伝導体 ,  最適化 ,  *イットリウムバリウム銅酸化物 ,  転移温度 ,  焼結 ,  磁気浮上 ,  スラリー ,  三次元 ,  *超伝導体 ,  熱処理条件 ,  *超伝導
準シソーラス用語： 熱処理温度 ,  高温処理 , 【Automatic Indexing@JST】

著者キーワード (4件)： 3Dプリンティング ,  押出自由形状成形 ,  バルクYBCO超伝導体 ,  複雑な形状

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (4件)： 押出し ,  YBCO ,  バルク ,  作製