PMMAの温度依存性機械的挙動:実験的解析とモデル化【Powered by NICT】

Temperature-dependent mechanical behaviour of PMMA: Experimental analysis and modelling

著者 (5件)： Abdel-Wahab Adel A. (Mechanical Engineering Department, Faculty of Engineering, Alexandria University, Alexandria, 21544, Egypt) ,  Abdel-Wahab Adel A. (Mechanical Engineering Department, College of Engineering, Al Imam Mohammad Ibn Saud Islamic University, Riyadh 11432, Saudi Arabia) ,  Ataya Sabbah (Department of Metallurgy and Materials Engineering, Faculty of Petroleum and Mining Engineering, Suez University, Suez, 43721, Egypt) ,  Ataya Sabbah (Mechanical Engineering Department, College of Engineering, Al Imam Mohammad Ibn Saud Islamic University, Riyadh 11432, Saudi Arabia) ,  Silberschmidt Vadim V. (Wolfson School of Mechanical, Electrical and Manufacturing Engineering, Loughborough University, Loughborough Leicestershire LE11 3TU, UK)
資料名： Polymer Testing  (Polymer Testing)
巻： 58  ページ： 86-95  発行年： 2017年 
JST資料番号： C0752B  ISSN： 0142-9418  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ポリメタクリル酸メチル(PMMA)の温度に依存した機械的挙動の実験的研究は,単軸引張と三点曲げ荷重条件下でそのガラス転移点(108 °C)以下の範囲の温度(20°C,40°C,60°Cおよび80°C)で行った。本研究では,二つの異なる構成材料モデルのための材料パラメータの同定を目的としたシミュレーションを伴っていた。PMMAに対して得られた実験的流れ曲線は弾塑性解析に用いたが,simフロー最適化ツールは,二層粘塑性モデルを採用した。温度はPMMAの有意な影響を受け機械的挙動を増加させ,80°Cで室温と超塑性挙動(ε>110%)準脆性破壊二層粘塑性材料モデルを弾塑性記述よりも一軸引張に対して得られた実験データと良く一致することが分かった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *モデリング ,  脆性破壊 ,  曲げ荷重 ,  *温度依存性 ,  粘塑性 ,  一軸 ,  弾塑性 ,  弾塑性解析 ,  引張 ,  *ポリメタクリル酸メチル ,  最適化
準シソーラス用語： 粘塑性モデル ,  二層 ,  材料パラメータ ,  *力学的挙動 , 【Automatic Indexing@JST】

著者キーワード (6件)： ポリ(メタクリル酸メチル) ,  一軸引張 ,  3点曲げ ,  温度依存性 ,  有限要素 ,  2層粘塑性