低圧コールドスプレーCoNiCrAlY被覆の高温腐食挙動

Hot Corrosion Behavior of Low-Pressure Cold-Sprayed CoNiCrAlY Coatings

著者 (5件)： Zhang L. W. (Jiangxi Key Laboratory for Advanced Copper and Tungsten Materials, Jiangxi Academy of Sciences, Nanchang, China) ,  Ning X. J. (National Key Laboratory of Science and Technology on Materials Under Shock and Impact, Beijing Institute of Technology, Beijing, China) ,  Lu L. (Jiangxi Key Laboratory for Advanced Copper and Tungsten Materials, Jiangxi Academy of Sciences, Nanchang, China) ,  Wang Q. S. (National Key Laboratory of Science and Technology on Materials Under Shock and Impact, Beijing Institute of Technology, Beijing, China) ,  Wang L. (National Key Laboratory of Science and Technology on Materials Under Shock and Impact, Beijing Institute of Technology, Beijing, China)
資料名： Journal of Thermal Spray Technology  (Journal of Thermal Spray Technology)
巻： 25  号： 3  ページ： 587-594  発行年： 2016年02月 
JST資料番号： W0482A  ISSN： 1059-9630  CODEN： JTTEE5  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： CoNiCrAlY被覆を低圧コールドスプレーで堆積させ真空環境において予備酸化し,その純粋なNa₂SO₄および75wt%Na₂SO₄+25wt%NaCl塩中での高温腐食を調べた。予備酸化処理はこの被覆表面上に緻密で連続なα-Al₂O₃スケールの形成をもたらした。900°C,150hで腐食させた後,予備酸化被覆は両方の塩に対して溶射したままの被覆よりも良好な耐食性を示した。生成したAl₂O₃スケールの存在は,内部酸化物および硫化物の形成を遅らせより緻密でより高い密着性のAl₂O₃スケールの形成を促進することでアルミニウムの消費速度を低減させた。さらに,コールドスプレーCoNiCrAlY被覆の二つの塩中での腐食機構を調べ,予備酸化処理の効果を議論した。Copyright 2016 ASM International Translated from English into Japanese by JST.

シソーラス用語： *コバルト合金 ,  ニッケル含有合金 ,  クロム含有合金 ,  アルミニウム含有合金 ,  イットリウム含有合金 ,  酸化 ,  *高温腐食 ,  *コールドスプレー ,  酸化膜 ,  耐食性
準シソーラス用語： 予備酸化

著者キーワード (5件)： cold spray ,  hot corrosion ,  MCrAlY coating ,  oxidation ,  pre-oxidation