SAC-フライアッシュ-再生微粉発泡系の性能【JST・京大機械翻訳】

Performance of SAC-ash/Recycled Powder Foaming System

著者 (5件)： Zhang Xiuqin (Collaborative Innovation Center of Engineering Construction and Safety in Shandong Blue Economic Zone,School of Civil Engineering,Qingdao Technological University) ,  Li Qiuyi (Collaborative Innovation Center of Engineering Construction and Safety in Shandong Blue Economic Zone,School of Civil Engineering,Qingdao Technological University) ,  Zang Jiakai (Xi’an University of Technology,School of Civil Engineering) ,  Zhang Yana (Collaborative Innovation Center of Engineering Construction and Safety in Shandong Blue Economic Zone,School of Civil Engineering,Qingdao Technological University) ,  Kong Zhe (Collaborative Innovation Center of Engineering Construction and Safety in Shandong Blue Economic Zone,School of Civil Engineering,Qingdao Technological University)
資料名： Cailiao Kexue Yu Gongcheng Xuebao  (Cailiao Kexue Yu Gongcheng Xuebao)
巻： 34  号： 5  ページ： 805-810  発行年： 2016年 
JST資料番号： C2657A  ISSN： 1673-2812  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 複合材料としてのアルミン酸塩セメント,フライアッシュ,および再生微粉体を,過酸化水素発泡によって調製した。発泡セメントの細孔径,圧縮強さ,および圧縮強さに及ぼす発泡剤量と再生剤の影響を研究し,発泡密度と圧縮強さの間の関係を研究した。実験結果は以下を示す。再生セメント量が同じ場合には,発泡セメントの圧縮強さと圧縮強さは共に増加したが,発泡セメントの気孔孔径は増加した。発泡剤の量が同じ場合には,干表観の密度,圧縮強さ及び気孔再生率は増加したが,干表観の気孔密度及び気孔孔径の減少幅は小さかった。発泡セメントの圧縮強度と圧縮強度は良好な直線相関を示し,R2は0.96936であった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： セメント ,  発泡剤 ,  *起泡 ,  過酸化水素 ,  複合材料 ,  細孔径 ,  *フライアッシュ ,  気孔 ,  アルミン酸塩 ,  圧縮強さ ,  *微粉体
準シソーラス用語： 気孔密度 , 【Automatic Indexing@JST】

著者キーワード (5件)： foam cement ,  recycled powder ,  pore size ,  compressive strength ,  dry apparent density