Inhibitory effect of Ni-P coating on thermal expansion of carbon steel

著者 (5件)： Yang Yinghui (Key Laboratory for Liquid-solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061, China) ,  Liu Shuai (Key Laboratory for Liquid-solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061, China) ,  Li Jianguo (School of Materials Science and Engineering, Tsinghua University, Beijing 100062, China) ,  Bian Xiufang (Key Laboratory for Liquid-solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061, China) ,  Guo Zhilin (Key Laboratory for Liquid-solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061, China)
資料名： Surface & Coatings Technology  (Surface & Coatings Technology)
巻： 315  ページ： 484-489  発行年： 2017年 
JST資料番号： D0205C  ISSN： 0257-8972  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 炭素鋼の熱膨張は無電解メッキしたNi-P被覆により阻害された。試料の直径はめっき後にのみ3%増加した。基板の熱膨張(CTE)の線形係数は20.72%の還元速度と16ppm/Kから12.68ppmに減少した。613Kでは,Ni-P被覆は基板の熱膨張を抑制する一部体積収縮で結晶化し,従って,この方法で小さなCTE,結晶化補償機構と呼ばれるを誘導する。結晶化後,NiFeアンバ合金の一次相の一つであるFeNi_3から成る拡散層がコーティングと基板の界面でのその場を生成する。この拡散層は鉄基板の熱膨張,拡散層阻害機構と呼ばれるを阻害することにおいて重要な役割を果たす。これらの知見は,原理的に,全ての鉄合金に応用可能な有望な容易な方法は,鉄合金のCTEを減少させるために促進することができた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 拡散層 ,  無電解めっき ,  鉄合金 ,  *炭素鋼 ,  界面 ,  めっき ,  結晶化 ,  *熱膨張 ,  鉄 ,  線形性 ,  アンバ ,  *被覆
準シソーラス用語： 体積収縮 ,  還元速度 , 【Automatic Indexing@JST】

著者キーワード (4件)： 熱膨張 ,  Ni-P被覆 ,  無電解めっき ,  拡大阻害機構

分類 (5件)： 腐食  (WB03030B) ,  防食  (WB03040M) ,  金属材料へのセラミック被覆  (YC02050V) ,  拡散浸透めっき  (WC08025J) ,  気相めっき  (WC08022K)

タイトルに関連する用語 (4件)： 炭素鋼 ,  熱膨張 ,  Ni ,  阻害効果