SO_4(2-)/TIO_2固体超酸の安定性に及ぼす焼成温度の影響を研究した。【JST・京大機械翻訳】

Influence of calcination temperature on the water-resistant stability of SO_4(2-) / TiO_2 solid superacid

著者 (9件)： Li Licheng (College of Chemical Engineering, Nanjing Forestry University) ,  Hu Di (College of Chemical Engineering, Nanjing Forestry University) ,  Zhao Xuejuan (School of Materials Science and Engineering, Nanjing Institute of Technology) ,  Qian Qi (College of Chemical Engineering, Nanjing Forestry University) ,  Wang Lei (College of Chemical Engineering, Nanjing Forestry University) ,  Song Shanshan (College of Chemical Engineering, Nanjing Forestry University) ,  Yu Sifan (College of Chemical Engineering, Nanjing Forestry University) ,  Yan Jun (College of Chemical Engineering, Nanjing Forestry University) ,  Li Xiaobao (College of Chemical Engineering, Nanjing Forestry University)
資料名： Nanjing Linye Daxue Xuebao. Ziran Kexue Ban  (Nanjing Linye Daxue Xuebao. Ziran Kexue Ban)
巻： 40  号： 6  ページ： 129-134  発行年： 2016年 
JST資料番号： C2601A  ISSN： 1000-2006  CODEN： NLDXBZ  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 種々の焼成温度で調製したSO_4(2-)/TIO_2固体超酸の水熱安定性を,水熱処理によって研究し,XRD,NH_3-TPD,FT-IR,TG,およびBETによって特性評価した。結果は,焼成温度が500°C以下のとき,SO_4(2-)/TIO_2固体超酸の性能が類似していることを示した。焼成温度が600°C以上に上昇すると,SO_4(2-)/TIO_2の細孔構造は崩壊し,SO_4(2-)含有量は減少し,エステル化特性は著しく低下した。前処理の後,すべての固体超酸のエステル化活性は減少し,それはSO_4(2-)の脱着と酸量の減少に関連していた。400°Cで調製したSO_4(2-)/TIO_2固体超酸触媒は,より良い安定性を示した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： キャラクタリゼーション ,  酸性度 ,  細孔構造 ,  *エステル化 ,  前処理
準シソーラス用語： 酸触媒 ,  水熱処理 ,  水熱安定性 ,  *焼成温度 ,  *超酸 , 【Automatic Indexing@JST】

著者キーワード (4件)： SO_4(2-) / TiO_2 ,  solid superacid ,  calcination temperature ,  water resistant stability