700°Cの超臨界ボイラの腐食挙動に及ぼす硫黄含有量の影響を研究した。【JST・京大機械翻訳】

Effect of Sulfur Content on Corrosion Behavior of Candidate Alloys Used for 700 °C Level A-USC Boiler in Simulated Coal Ash and Flue Gas Environments

著者 (5件)： Li Yan (National Energy R&D Center of Clean and High-efficiency Fossil-fired Power Generation Technology, Xi′an Thermal Power Research Institute Co., Ltd.) ,  Lu Jintao (National Energy R&D Center of Clean and High-efficiency Fossil-fired Power Generation Technology, Xi′an Thermal Power Research Institute Co., Ltd.) ,  Yang Zhen (National Energy R&D Center of Clean and High-efficiency Fossil-fired Power Generation Technology, Xi′an Thermal Power Research Institute Co., Ltd.) ,  Zhu Ming (College of Materials Science and Engineering, Xi′an University of Science and Technology) ,  Gu Yuefeng (National Energy R&D Center of Clean and High-efficiency Fossil-fired Power Generation Technology, Xi′an Thermal Power Research Institute Co., Ltd.)
資料名： Zhongguo Fushi yu Fanghu Xuebao  (Zhongguo Fushi yu Fanghu Xuebao)
巻： 36  号： 5  ページ： 505-512  発行年： 2016年 
JST資料番号： W0862A  ISSN： 1005-4537  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 2つの典型的先進的超臨界蒸気ボイラのNI-COベース合金と,NI-FEベース合金GHGHの熱腐食挙動を,異なる硫黄含有量の模擬ボイラの煙道ガスと煙道ガス環境において研究した。結果は以下を示す。0.02%のSO_2雰囲気中では,2つの合金の腐食速度はより小さく,腐食速度はより良く,腐食速度はより低かった。1.5%のSO_2雰囲気中では,2つの合金の腐食速度は明らかに加速し,腐食層が著しく厚くなり,破裂剥離が発生し,腐食速度が悪化した。2つのS含有量雰囲気中で,合金の腐食生成物は基本的に同じであった。CCA 617の腐食生成物は主にCR_2O_3であり、少量の(NI、CO)CR_2O_4、AL_2O_3と硫化物である。GH 合金は,主にFE_2O_3,CR_2O_3,少量のNICR_2O_4および硫化物であった。実験結果に基づき,2つの合金の腐食機構とS含有量が合金の腐食過程に及ぼす影響について議論した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 蒸気ボイラ ,  *腐食 ,  *ボイラ ,  合金 ,  腐食生成物 ,  煙道ガス ,  腐食機構 ,  *硫黄 ,  腐食速度 ,  *超臨界
準シソーラス用語： *腐食挙動 , 【Automatic Indexing@JST】