増強された多重フェロイック性質をもつ結晶化したBi_0 9La_0 1Fe_0Cu3O6.95Mn_0 0.05O_3/Ba_0 7Sr_0 3Ti_0Cu3O6.95Co_0 0.05O_3二層薄膜【Powered by NICT】

Crystallized Bi_0.9La_0.1Fe_0.95Mn_0.05O₃/Ba_0.7Sr_0.3Ti_0.95Co_0.05O₃ bilayer thin films with enhanced multiferroic properties

著者 (6件)： Li Bin (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China) ,  Wang Chunqing (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China) ,  Wang Chunqing (Key Laboratory of Micro-systems and Micro-structures Manufacturing, Ministry of Education, Harbin Institute of Technology, Harbin 150080, China) ,  Dou Guangbin (Electrical and Electronic Engineering, Imperial College London, London SW7 2AZ, UK) ,  Wang Zhenbin (Department of Materials Science and Engineering, University of Science and Technology of China, Hefei 230026, China) ,  Fei Weidong (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China)
資料名： Applied Surface Science  (Applied Surface Science)
巻： 404  ページ： 162-167  発行年： 2017年 
JST資料番号： B0707B  ISSN： 0169-4332  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 増強マルチフェロイック特性およびバッファ層としてBa_0 7Sr_0 3Ti_0 0.95Co_0 0.05O_3(BSTCO)膜を用いた第二相を含まないBi_0 9La_0 1Fe_0 0.95Mn_0 0.05O_3(BLFMO)膜の合成を報告した。ゾル-ゲル法を用いて結晶化したBLFMO/BSTCO膜中の磁区が観察されたを調製し,不純物相は検出されなかった。バッファ層はBLFMO膜の飽和磁化と保持力値を効果的に強化できることを見出し,特にこれらの二層膜の保磁力は緩衝層のないBLFMO膜のそれより有意に強かった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： バッファ層 ,  不純物 ,  *薄膜 ,  保磁力 ,  第二相 ,  飽和磁化 ,  ゾル-ゲル法 ,  *多重化 ,  磁区 ,  *結晶化
準シソーラス用語： 二重層 ,  保持力 ,  磁性強誘電体 ,  *二層 , 【Automatic Indexing@JST】

著者キーワード (5件)： Multiferroics ,  強誘電性 ,  磁気的性質 ,  ペロブスカイト ,  薄膜

分類 (1件)： 酸化物薄膜  (BK14050P)

タイトルに関連する用語 (5件)： 増強 ,  多重 ,  性質 ,  結晶化 ,  薄膜