Experiment on Selective Laser Melting Forming of Al_2O_3 Ceramics

著者 (6件)： Zhang Kai (School of Mechanical Engineering, Nanjing University of Science and Technology, Jiangsu Engineering Laboratory of High-End Manufacturing Equipment and Technology) ,  Liu Tingting (School of Mechanical Engineering, Nanjing University of Science and Technology, Jiangsu Engineering Laboratory of High-End Manufacturing Equipment and Technology) ,  Liao Wenhe (School of Mechanical Engineering, Nanjing University of Science and Technology, Jiangsu Engineering Laboratory of High-End Manufacturing Equipment and Technology) ,  Zhang Changdong (School of Mechanical Engineering, Nanjing University of Science and Technology, Jiangsu Engineering Laboratory of High-End Manufacturing Equipment and Technology) ,  Yan Yishuai (School of Mechanical Engineering, Nanjing University of Science and Technology, Jiangsu Engineering Laboratory of High-End Manufacturing Equipment and Technology) ,  Du Daozhong (School of Mechanical Engineering, Nanjing University of Science and Technology, Jiangsu Engineering Laboratory of High-End Manufacturing Equipment and Technology)
資料名： Zhongguo Jiguang  (Zhongguo Jiguang)
巻： 43  号： 10  ページ： 1002007_01-1002007_7  発行年： 2016年 
JST資料番号： C5022A  ISSN： 0258-7025  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： AL_2O_3粉末とスラリーの基本的実験的研究をレーザ誘起溶融技術によって実施した。実験結果は,AL_2O_3粉末の成形効果がより悪く,AL_2O_3スラリーがより良い効果を持つことを示した。レーザ出力はAL_2O_3スラリーの表面品質に重要な影響を及ぼし,表面品質はレーザパワーの増加とともに増加した。レーザ出力が200W,走査速度が90MM/Sのとき,AL_2O_3試料のビッカース硬さは約14.7GPAであった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： レーザ出力 ,  粉体 ,  表面性状 ,  *スラリー
準シソーラス用語： Vickers硬さ ,  走査速度 ,  実験研究 ,  *レーザ誘起 , 【Automatic Indexing@JST】

著者キーワード (4件)： laser technique ,  selective laser melting ,  Al_2O_3 ceramic ,  slurry

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (4件)： アルミナセラミックス ,  レーザ誘起 ,  溶融 ,  実験