火山灰に基づいたジオポリマーモルタルの機械的性質と耐久性【Powered by NICT】

Mechanical properties and durability of volcanic ash based geopolymer mortars

著者 (5件)： Yankwa Djobo Jean Noeel (Laboratory of Applied Inorganic Chemistry, Department of Inorganic Chemistry, Faculty of Science, University of Yaounde I, P.O. Box 812, Yaounde, Cameroon) ,  Yankwa Djobo Jean Noeel (CSIR-National Metallurgical Laboratory, Jamshedpur 831007, India) ,  Elimbi Antoine (Laboratory of Applied Inorganic Chemistry, Department of Inorganic Chemistry, Faculty of Science, University of Yaounde I, P.O. Box 812, Yaounde, Cameroon) ,  Kouamo Tchakoute Herve (Laboratory of Applied Inorganic Chemistry, Department of Inorganic Chemistry, Faculty of Science, University of Yaounde I, P.O. Box 812, Yaounde, Cameroon) ,  Kumar Sanjay (CSIR-National Metallurgical Laboratory, Jamshedpur 831007, India)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 124  ページ： 606-614  発行年： 2016年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 27°Cと80°Cで合成した火山灰ベースのジオポリマーモルタルの機械的性質と耐久性を評価した。水吸収,見掛けの多孔性28日まで,増加は時間とともにほぼ一定となった。27°Cで養生した試験体のバルク密度は時間とともに連続的に減少したが,80°Cで養生した試験体に対して時間と共にかなり変化しない27°Cで硬化したジオポリマー試料は28日後に20.5MPaの圧縮強度を達成し,それは,より長い時間と共に有意に増加しなかった。が80°Cで養生した試験体では90日で達成された。37.9MPaの最大強度試料は湿潤と乾燥条件で良い性能を示した。27°Cで得られたジオポリマー試料は80°Cで硬化させた場合より5%硫酸に対する良好な抵抗性を開発した。酸曝露後のジオポリマー試料の微細構造は,ジオポリマーゲルからの硫酸とカルシウムの間の反応による二次相としての石膏の形成を明らかにした。27°Cで硬化した試料中のNaに富むゲルの存在はその酸抵抗性を高める。細孔構造と透過性は火山灰ベースのジオポリマーモルタルの耐久性に影響する重要な因子である。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 細孔構造 ,  多孔性 ,  ナトリウム ,  *火山灰 ,  カルシウム ,  容積重 ,  ゲル ,  湿潤 ,  第二相 ,  耐酸性 ,  硫酸 ,  *耐久性 ,  石膏 ,  圧縮強さ ,  *ジオポリマ ,  機械的性質 ,  強度

著者キーワード (5件)： 機械的性質 ,  耐久性 ,  火山灰 ,  ジオポリマー ,  硬化温度