文献

J-GLOBAL ID：201702270584530926   整理番号：17A0407660

高圧焼結法により作製したp型Nd_1in_Te_3の熱電性能【Powered by NICT】

Thermoelectric performance of p-type Nd_1- In Te₃ fabricated by high pressure sintering method

著者 (6件)： Mao Tao (Department of Inorganic Non-metal Materials, University of Science and Technology Beijing, Beijing 100083, China) ,  Ren Pan (Department of Inorganic Non-metal Materials, University of Science and Technology Beijing, Beijing 100083, China) ,  Xu Guiying (Department of Inorganic Non-metal Materials, University of Science and Technology Beijing, Beijing 100083, China) ,  Gao Junling (Department of Inorganic Non-metal Materials, University of Science and Technology Beijing, Beijing 100083, China) ,  Di Jiaxin (Department of Inorganic Non-metal Materials, University of Science and Technology Beijing, Beijing 100083, China) ,  Zhang Libo (Department of Inorganic Non-metal Materials, University of Science and Technology Beijing, Beijing 100083, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 696  ページ： 648-654  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 高圧焼結法により作製したNd_1で_Te_3(x=0,0.01,0.03,0.05)の熱電特性を291K,673Kの温度範囲で調べた。結果は623K400K以上で,中程度にドープしたNd_1で_Te_3(0.01,0.03と0.05)の熱伝導率は非ドープNdTe_3の合金散乱に起因すると考えられるよりも40%~ 50%低いことを示した。力率の絶対値は,ドーピングによって若干減少していたが,熱伝導率の低下は,623Kで高いZTをもたらす特に,軽度にInをドープした化合物Nd_0 0.99In_0 0.01Te_3は最良の熱電性能を示し,623Kで0.18のZT性能指数これは本研究で測定した非ドープNdTe_3のそれの2倍である,NdTe_3における適切なInドーピングはその熱電性能を改善するための有望な方法であることを示唆した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 熱伝導率 ,  絶対値 ,  合金 ,  インジウム ,  散乱 ,  *高圧 ,  性能指数 ,  ドーピング ,  力率 ,  *焼結
準シソーラス用語： 温度範囲 ,  熱電特性 , 【Automatic Indexing@JST】

著者キーワード (3件)： Nd_1inは_Te_3 ,  高圧焼結 ,  熱電特性

分類 (2件)： 電気的性質  (WB02010Y) ,  セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (2件)： 高圧 ,  作製