超音速アーク溶射によって調製したFECRNI複合被膜の微細構造と特性を研究した。【JST・京大機械翻訳】

Microstructure and properties of FeCrNi composite coating sprayed by high velocity arc

著者 (6件)： Wu Yanming (Standard and Quality Control Research Institute, Hydraulic Machinery and Remanufacturing Technology Engineering Laboratory of Zhejiang Province) ,  Zhao Jian (Standard and Quality Control Research Institute, Hydraulic Machinery and Remanufacturing Technology Engineering Laboratory of Zhejiang Province) ,  Chen Xiaoming (Standard and Quality Control Research Institute, Hydraulic Machinery and Remanufacturing Technology Engineering Laboratory of Zhejiang Province) ,  Fu Li (Standard and Quality Control Research Institute) ,  Mao Pengzhan (Standard and Quality Control Research Institute, Hydraulic Machinery and Remanufacturing Technology Engineering Laboratory of Zhejiang Province) ,  Liu Wei (Hydraulic Machinery and Remanufacturing Technology Engineering Laboratory of Zhejiang Province, Hangzhou Mechanical Research Institute)
資料名： Cailiao Rechuli Xuebao  (Cailiao Rechuli Xuebao)
巻： 37  号： 9  ページ： 178-182  発行年： 2016年 
JST資料番号： C2127A  ISSN： 1009-6264  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 超音速アーク溶射(HV-ARC)技術を用いて,Q235鋼の表面上にFECRNI複合被覆を調製した。被覆の微細構造と特性を,走査型電子顕微鏡(SEM),X線回折(XRD),光学顕微鏡,微小硬さ試験機,摩擦摩耗試験機,および電気化学的ワークステーションによって研究した。結果は以下を示す。超音速アークの高エネルギーと高粒子速度は,コーティングの低い空隙率と高い結合強度をもたらす。コーティング中にCR,NIが存在し,これらの酸化被膜は硬さと耐摩耗性に大きな影響を及ぼす。超音速アーク溶射被覆の耐摩耗性は,通常のアーク溶射被覆のそれより40%以上高く,基材Q235鋼のそれより4.5倍以上増加し,耐食性も大幅に向上した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 付着強さ ,  火炎溶射 ,  耐食性 ,  粒子速度 ,  微小硬さ ,  硬度 ,  走査電子顕微鏡 ,  空隙率 ,  耐摩耗性 ,  *アーク放電 ,  X線回折 ,  *アーク溶射 ,  Q235鋼 ,  *複合被膜 ,  *超音速 ,  機械的性質 ,  耐性

著者キーワード (3件)： HV-ARC ,  FeCrNi composite coatings ,  property

分類 (1件)： 機械的性質  (WB02030U)

タイトルに関連する用語 (6件)： 超音速 ,  アーク溶射 ,  調製 ,  複合被膜 ,  微細構造 ,  研究