非ハロゲン化溶媒で被覆した高分子太陽電池スプレー【Powered by NICT】

Polymer solar cells spray coated with non-halogenated solvents

著者 (14件)： Cai Chaosheng (Siyuan Laboratory, Guangzhou Key Laboratory of Vacuum Coating Technologies and New Energy Materials, Key Laboratory of Optoelectronic Information and Sensing Technologies of Guangdong Higher Education Institutes, Department of Physics, Jinan University, Guangzhou 510632, PR China) ,  Zhang Yangdong (Siyuan Laboratory, Guangzhou Key Laboratory of Vacuum Coating Technologies and New Energy Materials, Key Laboratory of Optoelectronic Information and Sensing Technologies of Guangdong Higher Education Institutes, Department of Physics, Jinan University, Guangzhou 510632, PR China) ,  Song Rongying (Siyuan Laboratory, Guangzhou Key Laboratory of Vacuum Coating Technologies and New Energy Materials, Key Laboratory of Optoelectronic Information and Sensing Technologies of Guangdong Higher Education Institutes, Department of Physics, Jinan University, Guangzhou 510632, PR China) ,  Peng Zuosheng (Siyuan Laboratory, Guangzhou Key Laboratory of Vacuum Coating Technologies and New Energy Materials, Key Laboratory of Optoelectronic Information and Sensing Technologies of Guangdong Higher Education Institutes, Department of Physics, Jinan University, Guangzhou 510632, PR China) ,  Xia Lianpeng (Siyuan Laboratory, Guangzhou Key Laboratory of Vacuum Coating Technologies and New Energy Materials, Key Laboratory of Optoelectronic Information and Sensing Technologies of Guangdong Higher Education Institutes, Department of Physics, Jinan University, Guangzhou 510632, PR China) ,  Wu Mingxiao (Siyuan Laboratory, Guangzhou Key Laboratory of Vacuum Coating Technologies and New Energy Materials, Key Laboratory of Optoelectronic Information and Sensing Technologies of Guangdong Higher Education Institutes, Department of Physics, Jinan University, Guangzhou 510632, PR China) ,  Xiong Kang (Siyuan Laboratory, Guangzhou Key Laboratory of Vacuum Coating Technologies and New Energy Materials, Key Laboratory of Optoelectronic Information and Sensing Technologies of Guangdong Higher Education Institutes, Department of Physics, Jinan University, Guangzhou 510632, PR China) ,  Wang Biao (Siyuan Laboratory, Guangzhou Key Laboratory of Vacuum Coating Technologies and New Energy Materials, Key Laboratory of Optoelectronic Information and Sensing Technologies of Guangdong Higher Education Institutes, Department of Physics, Jinan University, Guangzhou 510632, PR China) ,  Lin Yuanbao (Siyuan Laboratory, Guangzhou Key Laboratory of Vacuum Coating Technologies and New Energy Materials, Key Laboratory of Optoelectronic Information and Sensing Technologies of Guangdong Higher Education Institutes, Department of Physics, Jinan University, Guangzhou 510632, PR China) ,  Xu Xiaofeng (Department of Chemistry and Chemical Engineering, Chalmers University of Technology, SE-412 96 Goteborg, Sweden) ,  Liang Quanbing (Institute of Polymer Optoelectronic Materials & Devices, State Key Laboratory of Luminescent Materials & Devices, South China University of Technology, Guangzhou 510640, PR China) ,  Wu Hongbin (Institute of Polymer Optoelectronic Materials & Devices, State Key Laboratory of Luminescent Materials & Devices, South China University of Technology, Guangzhou 510640, PR China) ,  Wang Ergang (Department of Chemistry and Chemical Engineering, Chalmers University of Technology, SE-412 96 Goteborg, Sweden) ,  Hou Lintao (Siyuan Laboratory, Guangzhou Key Laboratory of Vacuum Coating Technologies and New Energy Materials, Key Laboratory of Optoelectronic Information and Sensing Technologies of Guangdong Higher Education Institutes, Department of Physics, Jinan University, Guangzhou 510632, PR China)
資料名： Solar Energy Materials and Solar Cells  (Solar Energy Materials and Solar Cells)
巻： 161  ページ： 52-61  発行年： 2017年 
JST資料番号： D0513C  ISSN： 0927-0248  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： スプレーコーティング法を用いて,受容体として供与体と[6,6]-フェニルC_61酪酸メチルエステル(PC_61BM)または[6,6]-フェニルC_71酪酸メチルエステル(PC_71BM)として共役高分子ポリ[2,3-ビス-(3-オクチルオキシフェニル)キノキサリン-5,8-ジイル-alt-チオフェン-2,5-ジイル](TQ1)に基づく従来のITOと逆ITOフリー高分子太陽電池(PSC)を作製した。環境にやさしい非ハロゲン化溶媒を用いて,活性層を処理した。ITOベースTQ1:PC_61BM PSCsの光起電力性能に及ぼす基板温度と処理溶媒の影響を系統的に調べた。より高い基板温度は,溶媒蒸発速度を加速し,微小気孔配列組織を持つ粗い表面,光反射率と増強された吸収を効果的に減少させ,が可能である。さらに,この高い基板温度を用いた場合にはより繊細な相分離が観察され,これは減少した二分子再結合に起因する増強された光電流をもたらした。非ハロゲン化溶媒混合物を用いた噴霧加工PSCのデバイス性能はハロゲン化o-ジクロロベンゼン(oDCB)を用いた噴霧加工PSCの非ハロゲン化溶媒である噴霧加工PSCに非常に有望であることを実証すると同等であった。本研究では,環境に優しい溶媒を用いた効率的なロール・ツー・ロール適合スプレー被覆PSCの開発に新たな光を当てた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 基板温度 ,  スプレー塗装 ,  再結合 ,  活性層 ,  光電流 ,  光起電力 ,  *ハロゲン化 ,  光トラッピング ,  ドナー ,  噴霧
準シソーラス用語： ロール・ツー・ロール方式 ,  光反射率 ,  溶媒蒸発 ,  共役重合体 ,  *高分子太陽電池 , 【Automatic Indexing@JST】

著者キーワード (5件)： 高分子太陽電池 ,  スプレーコーティング ,  非ハロゲン化溶媒 ,  過渡溶媒蒸発 ,  光トラッピング

分類 (1件)： 太陽電池  (NC03084O)

タイトルに関連する用語 (3件)： 非ハロゲン化溶媒 ,  高分子太陽電池 ,  スプレー