Cu_2SnSe_3の熱電特性に及ぼす第二相の影響【Powered by NICT】

Effect of secondary phases on thermoelectric properties of Cu₂SnSe₃

著者 (15件)： Ma Rui (Key Laboratory of Cryogenics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, PR China) ,  Ma Rui (University of Chinese Academy of Sciences, Beijing 100049, PR China) ,  Liu Guanghua (Key Laboratory of Cryogenics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, PR China) ,  Liu Guanghua (State Key Laboratory of New Ceramics & Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084, PR China) ,  Li Jiangtao (Key Laboratory of Cryogenics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, PR China) ,  Li Jiangtao (State Key Laboratory of New Ceramics & Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084, PR China) ,  Li Yuyang (Key Laboratory of Cryogenics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, PR China) ,  Li Yuyang (State Key Laboratory of New Ceramics & Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084, PR China) ,  Chen Kexin (State Key Laboratory of New Ceramics & Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084, PR China) ,  Han Yemao (Key Laboratory of Cryogenics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, PR China) ,  Han Yemao (State Key Laboratory of New Ceramics & Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084, PR China) ,  Zhou Min (Key Laboratory of Cryogenics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, PR China) ,  Zhou Min (State Key Laboratory of New Ceramics & Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084, PR China) ,  Li Laifeng (Key Laboratory of Cryogenics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, PR China) ,  Li Laifeng (State Key Laboratory of New Ceramics & Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084, PR China)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： 9  ページ： 7002-7010  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 異なる二次相を有するCu_2SnSe_3試料はCu_xSnSe_3(x=1.8 2.2)とCu_2Sn_ySe_3(y=0.8 1.2)の組成から調製し,それらの熱電特性を調べた。Cu_xSnSe_3試料では,二次相はxが1.8と1.9とSnSe 2.2のSnSe_2であり,ほぼ単相のCu_2SnSe_3は2.0と2.1を得た。Cu_2Sn_ySe_3試料では,二次相はxが1.1と1.2のy=0.8とSnSeのためのCuSeであり,0.9と1.0で生産される単相Cu_2SnSe_3。合成Cu_2SnSe_3の格子構造は,xおよびy値に依存し,x>2.0またはy>1.0ではx≦2.0y≦1.0と単斜晶系の立方晶である。単相Cu_2SnSe_3試料(77_3KでZT=0.4_2)と比較して,SnSe_2二次相を有する試料は773Kで0.84の大幅に強化されたZT,これまで非ドープCu_2SnSe_3のための最良の結果と思われるを示した。SnSe二次相を有する試料は貧弱な熱電特性を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 格子構造 ,  単斜晶系 ,  *第二相 ,  *銅 ,  単相 ,  ドーピング
準シソーラス用語： *熱電特性 , 【Automatic Indexing@JST】

著者キーワード (4件)： 熱電特性 ,  Chalcogenides ,  Cu_2SnSe_3 ,  燃焼合成

分類 (4件)： セラミック・磁器の性質  (YC03030G) ,  圧電気,焦電気,エレクトレット  (BM05040M) ,  セラミック・陶磁器の製造  (YC03020V) ,  圧電デバイス  (NC03110I)

タイトルに関連する用語 (2件)： 熱電特性 ,  第二相