CuNiSi合金の機械的性質に及ぼす微細構造の影響【Powered by NICT】

Effects of microstructure on mechanical properties of CuNiSi alloys

著者 (7件)： Gholami M. (TU-Clausthal, Institute of Materials Science and Engineering, Clausthal-Zellerfeld, Germany) ,  Vesely J. (Charles University, Department of Physics of Materials, Prague, Czechia) ,  Altenberger I. (Wieland-Werke AG, Central Laboratory, Research & Development, Ulm, Germany) ,  Kuhn H.-A. (Wieland-Werke AG, Central Laboratory, Research & Development, Ulm, Germany) ,  Janecek M. (Charles University, Department of Physics of Materials, Prague, Czechia) ,  Wollmann M. (TU-Clausthal, Institute of Materials Science and Engineering, Clausthal-Zellerfeld, Germany) ,  Wagner L. (TU-Clausthal, Institute of Materials Science and Engineering, Clausthal-Zellerfeld, Germany)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 696  ページ： 201-212  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 産業における析出硬化したCu-Ni-Si合金に対する需要が増加している,高強度と中程度の電気伝導率が要求される。本研究の主目的は,スエージング(SW)を用いてミクロ組織微細化の組合せを適用したCu-2.5wt%Ni-0.5wt%Si-0.06wt%Mg(Cu 2.5Ni 0.5Si 0.06Mg),最適化された析出硬化に超微細結晶粒(UFG)ミクロ組織を生成することであった。その結果,析出硬化非スエージングしたサンブル(粗粒(CG)条件)と比較して,析出硬化後スエージングしたサンブル(UFG条件)の機械的特性のかなりの改善が明らかである。UFG状態の機械的性質はCG状態のものと有意に優れた,すなわち,14%の破壊と800 900MPaの引張強さと伸びの急激な増加が達成できた。本研究では,光学顕微鏡(OM),電子チャネリングコントラストイメージング(ECCI)法,および透過型電子顕微鏡(TEM)を用いて種々の処理工程後のミクロ組織の詳細な記述を要約し,強度と延性のような最も重要な機械的性質に及ぼす結果を提示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 光学顕微鏡 ,  電気伝導率 ,  微結晶 ,  析出硬化 ,  電子チャネリング ,  スエージ加工 ,  引張強さ ,  *合金 ,  透過型電子顕微鏡 ,  精密化 ,  *機械的性質 ,  伸び ,  延性 ,  最適化
準シソーラス用語： 高強度 , 【Automatic Indexing@JST】

著者キーワード (3件)： Cu-5Ni-5Si-0.06Mg合金 ,  析出硬化 ,  機械的性質

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)