ポリブテン-1繊維のモルフォロジーと結晶相転移を高圧静電紡糸によって調製した。【JST・京大機械翻訳】

Morphology and Polymorphic Transformation of an Electrospun Isotactic Poly(1-butene) Fibers via Electrospinning

著者 (3件)： Ma Yaping (Shandong Provincial Key Laboratory of Olefin Catalysis and Polymerization,Key Laboratory of Rubber-Plastics (Ministry of Education),School of Polymer Science and Engineering,Qingdao University of Science and Technology) ,  Shao Huafeng (Shandong Provincial Key Laboratory of Olefin Catalysis and Polymerization,Key Laboratory of Rubber-Plastics (Ministry of Education),School of Polymer Science and Engineering,Qingdao University of Science and Technology) ,  He Aihua (Shandong Provincial Key Laboratory of Olefin Catalysis and Polymerization,Key Laboratory of Rubber-Plastics (Ministry of Education),School of Polymer Science and Engineering,Qingdao University of Science and Technology)
資料名： Gaofenzi Cailiao Kexue yu Gongcheng  (Gaofenzi Cailiao Kexue yu Gongcheng)
巻： 32  号： 8  ページ： 86-92  発行年： 2016年 
JST資料番号： C2119A  ISSN： 1000-7555  CODEN： GCKGEI  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： ポリブテン-1のシクロヘキサン溶液を高圧静電紡糸により調製し,光学顕微鏡,走査型電子顕微鏡,FOURIER変換赤外分光法,X線回折により特性評価した。また,紡糸過程と室温でのねかし繊維の結晶相転移についても研究した。結果により、紡糸液の濃度と推進速度の増加につれて、均一なサイズの繊維が得られ、直径も大きくなることが分かった。紡糸電圧が増加すると,繊維直径は減少したが,繊維直径分布は均一になった。一次ポリブテン-1紡糸膜の結晶相はI型とII型であり,溶媒の揮発と時間の延長により結晶相IIは結晶相Iに徐々に変換し,溶液相は結晶相IIIと結晶I’になった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *エレクトロスピニング ,  *結晶 ,  液相 ,  X線回折 ,  *相転移 ,  光学顕微鏡 ,  キャラクタリゼーション ,  *高圧 ,  走査電子顕微鏡 ,  *モルフォロジー ,  *紡糸 ,  シクロアルカン
準シソーラス用語： *結晶相 ,  直径分布 ,  紡糸液 , 【Automatic Indexing@JST】

著者キーワード (5件)： poly(1-butene) ,  electro-spinning ,  crystalline transformation ,  fibers ,  morphology

分類 (3件)： 多糖類  (CF10054P) ,  塩基,金属酸化物  (CD01030Z) ,  高分子固体の物理的性質  (CG02024U)

物質索引 (1件)： シクロヘキサン

タイトルに関連する用語 (7件)： ポリブテン ,  繊維 ,  モルフォロジー ,  結晶相 ,  高圧 ,  静電紡糸 ,  調製