SiC被覆C/C複合材料のZrSi_2CrSi_2SiC多相被覆のミクロ組織と熱特性に及ぼすCr含有量の影響【Powered by NICT】

Effect of Cr content on the microstructure and thermal properties of ZrSi₂-CrSi₂-SiC multiphase coating for the SiC coated C/C composites

著者 (4件)： Hu Manhong (State Key Laboratory of Solidification Processing, Carbon/Carbon Composites Research Center, Northwestern Polytechnical University, Xi’an 710072, China) ,  Hu Manhong (College of Mechanical and Electrical Engineering, North University of China, Taiyuan 030051, China) ,  Li Kezhi (State Key Laboratory of Solidification Processing, Carbon/Carbon Composites Research Center, Northwestern Polytechnical University, Xi’an 710072, China) ,  Wang Jing (College of Mechanical and Electrical Engineering, North University of China, Taiyuan 030051, China)
資料名： Ceramics International  (Ceramics International)
巻： 42  号： 16  ページ： 19357-19364  発行年： 2016年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 一連のパック粉末中の種々のCr量のZrSi_2CrSi_2SiC多相被覆のアルゴンでのパックセメンテーションによるSiC被覆炭素/炭素(C/C)複合材料の表面上に作製した。多相被覆の相組成,微細構造及びスポット要素をX線回折,走査電子顕微鏡およびエネルギー分散分光法によって分析した。多相被覆の微細構造,耐酸化性と耐熱衝撃性に及ぼすCr含有量の影響を調べた。結果はCr含有量の増加と共に,CrSi_2相の含有量と被覆中の亀裂の数とサイズが増加することを示した。Cr含有量10wt%で調製したZrSi_2CrSi_2SiC多相被覆は最良の耐酸化性と耐熱衝撃性を示した。試料の重量損失は1500°Cで115時間の酸化後0.84%であり,体重増加は1500°Cと室温の間の50回の熱サイクル後0.66%であった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 走査電子顕微鏡 ,  *クロム ,  相組成 ,  *C/C複合材料 ,  熱サイクル ,  重量損失 ,  *多相 ,  耐酸化性 ,  アルゴン ,  *炭化ケイ素 ,  X線回折 ,  *熱特性 ,  耐熱衝撃性 ,  *被覆
準シソーラス用語： パックセメンテーション , 【Automatic Indexing@JST】

著者キーワード (4件)： 炭素/炭素複合材料 ,  耐酸化性 ,  多相被覆 ,  CrSi_2

分類 (2件)： 非金属材料へのセラミック被覆  (YC02040K) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (6件)： SiC ,  複合材料 ,  多相 ,  ミクロ組織 ,  熱特性 ,  Cr含有量