3種類のマンドレル鋼の熱疲労特性を比較した。【JST・京大機械翻訳】

Comparison of Thermo-fatigue Properties of Three Type Mandrel Alloying Steels

著者 (3件)： He Xijuan (School of Materials Science and Engineering, Shanghai University, State Key Laboratory of Metallurgy and Preparation of Advanced Special Steel Built by Province and Ministry, Shanghai Key Laboratory of Advanced Ferrometallurgy) ,  Zuo Pengpeng (School of Materials Science and Engineering, Shanghai University, State Key Laboratory of Metallurgy and Preparation of Advanced Special Steel Built by Province and Ministry, Shanghai Key Laboratory of Advanced Ferrometallurgy) ,  Wu Xiaochun (School of Materials Science and Engineering, Shanghai University, State Key Laboratory of Metallurgy and Preparation of Advanced Special Steel Built by Province and Ministry, Shanghai Key Laboratory of Advanced Ferrometallurgy)
資料名： Rejiagong Gongyi  (Rejiagong Gongyi)
巻： 45  号： 18  ページ： 120-123,126  発行年： 2016年 
JST資料番号： C2487A  ISSN： 1001-3814  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 自己拘束熱疲労試験法を用いて,3種類のマンドレル鋼の熱疲労特性を,変倍体視の顕微鏡およびMH-3型の微小硬さ試験機によって研究した。熱疲労亀裂の発生,拡大と材料靭性の間の関係を分析した。結果により,TBX-1鋼およびTBX-4鋼の熱疲労亀裂発生は,400サイクルのサイクル数で,H13鋼のそれより早かった。3000回のサイクル後,TBX-4鋼は良好な熱疲労特性を示し,疲労損傷因子はTBX-1鋼とH13鋼より明らかに低く,熱疲労抵抗はTBX-1鋼とH13鋼よりも優れていた。3種類の鋼の熱疲労機構を解析し,材料の熱疲労亀裂抵抗を決定する主要因は鋼の衝撃靭性であることを指摘した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 耐亀裂性 ,  微小硬さ ,  試験装置 ,  亀裂 ,  *マンドレル ,  疲れ損傷 ,  顕微鏡 ,  靱性 ,  *鋼
準シソーラス用語： 衝撃靱性 ,  AISIH13 ,  試験方法 ,  *熱疲労 , 【Automatic Indexing@JST】

著者キーワード (5件)： mandrel alloying steels ,  thermo fatigue properties ,  fatigue damage factor ,  crack initiation ,  crack expansion