粉末冶金と熱間押出技術によるナノSiC/2014Al複合材料の時効挙動【Powered by NICT】

Aging Behavior of Nano-SiC/2014Al Composite Fabricated by Powder Metallurgy and Hot Extrusion Techniques

著者 (7件)： Wang Zhiguo (School of Materials Science and Engineering, Nanling Campus, Jilin University) ,  Li Chuanpeng (School of Materials Science and Engineering, Nanling Campus, Jilin University) ,  Wang Huiyuan (School of Materials Science and Engineering, Nanling Campus, Jilin University) ,  Zhu Xian (School of Materials Science and Engineering, Nanling Campus, Jilin University) ,  Wu Min (School of Materials Science and Engineering, Nanling Campus, Jilin University) ,  Li Jiehua (Chair of Casting Research, Montanuniversitaet Leoben) ,  Jiang Qichuan (School of Materials Science and Engineering, Nanling Campus, Jilin University)
資料名： Journal of Materials Science & Technology  (Journal of Materials Science & Technology)
巻： 32  号： 10  ページ： 1008-1012  発行年： 2016年 
JST資料番号： T0871A  ISSN： 1005-0302  CODEN： JSCTEQ  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： 粉末冶金加工した2014Al合金とその複合材料の時効硬化速度論を研究した。n-SiC粒子の存在はピーク硬さの増加をもたらした。興味深いことに,複合材料のaginghardeningピークは非強化合金のそれよりも早い時間で起こった。透過型電子顕微鏡(TEM)研究は,主要な析出相はAl_5Cu_2Mn_3とθ′(Al_2Cu)であることを示した。に加えて,ピーク硬化条件,Agなしのアルミニウム金属基複合材料における以前に観察されたほとんどの両方で試験片に現れたΩ相。加速時効速度とピーク硬さの増加はSiCと2014Al母相の間の熱膨張係数のミスマッチから生じたより高い転位密度に起因すると考えられる。結果はピストン,駆動軸管,ブレーキロータ,自転車フレーム,鉄道ブレーキなどの自動車分野への応用のための高性能複合材料を作製するための有益である。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： *熱間押出 ,  ブレーキ ,  時効硬化 ,  ピストン ,  透過型電子顕微鏡 ,  *炭化ケイ素 ,  熱膨張係数 ,  *アルミニウム ,  *複合材料 ,  不整合 ,  硬度 ,  *粉末冶金 ,  金属基複合材料 ,  *時効 ,  転位密度

著者キーワード (5件)： 金属マトリックス複合材料 ,  ナノSiC ,  粉末冶金 ,  熱間押出 ,  時効硬化

分類 (1件)： 分散強化合金  (WE04030R)

タイトルに関連する用語 (6件)： 粉末冶金 ,  熱間押出 ,  SiC ,  複合材料 ,  時効 ,  挙動