Effect of Short-Aging Treatment on Microstructure and Micro-hardness of HR3C Alloy

著者 (5件)： Hou Benrui (College of Materials Science and Engineering, Xi’an University of Science and Technology, National Engineering Research Center of Clean Combustion in Power Generation) ,  Zhao Xinbao (National Engineering Research Center of Clean Combustion in Power Generation, Xi’an Thermal Power Research Institute Co., Ltd.) ,  Du Shuangming (College of Materials Science and Engineering, Xi’an University of Science and Technology) ,  Dang Yingying (National Engineering Research Center of Clean Combustion in Power Generation, Xi’an Thermal Power Research Institute Co., Ltd.) ,  Gu Yuefeng (National Engineering Research Center of Clean Combustion in Power Generation, Xi’an Thermal Power Research Institute Co., Ltd.)
資料名： Rejiagong Gongyi  (Rejiagong Gongyi)
巻： 45  号： 18  ページ： 245-248,251  発行年： 2016年 
JST資料番号： C2487A  ISSN： 1001-3814  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： HR3C合金の微細構造と微小硬さに及ぼす短期時効処理の影響を研究した。結果は以下を示す。合金を600~750°Cでそれぞれ1,5時間時効すると,結晶粒度は1200°C/30分の溶体化処理の後に著しく減少した。時効温度が上昇すると,結晶粒度はわずかに減少し,5H時効後に減少した。短期時効中に,HR3C粒界上にM_(23)C_6炭化物が析出し,保持温度の上昇と保持時間の延長により,炭化物の量はわずかに増加し,サイズはほとんど変化しなかった。同時に,ナノZ相は核内で核形成し成長した。固溶体と比較して,短期時効処理の後,合金の微小硬さは増加した。保持時間を長くすると,合金の微小硬さは安定に保たれる。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 溶体化処理 ,  微細構造 ,  結晶粒界 ,  核形成 ,  *時効 ,  炭化物 ,  *合金 ,  固溶体 ,  結晶粒度 ,  保持時間 ,  *微小硬さ
準シソーラス用語： Z相 , 【Automatic Indexing@JST】

著者キーワード (4件)： HR3C alloy ,  aging treatment ,  microstructure ,  micro-hardness

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  組織的硬化現象  (WB01020C)