極低温(77K)でのZTAセラミックの強靭化機構【Powered by NICT】

Toughening mechanisms of ZTA ceramics at cryogenic temperature (77K)

著者 (4件)： Chen Juan (State Key Laboratory of New Ceramics and Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084, PR China) ,  Xie Zhipeng (State Key Laboratory of New Ceramics and Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084, PR China) ,  Zeng Weining (State Key Laboratory of New Ceramics and Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084, PR China) ,  Wu Weiwei (State Key Laboratory of New Ceramics and Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084, PR China)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： 5  ページ： 3970-3974  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 20wt%ZrO_2を含むZTAセラミックはSPSとHPプロセスにより種々の焼結温度(1450°C,1500°C,1550°C)で作製した。298Kおよび77KにおけるZTAセラミックの機械的性質に及ぼす焼結プロセスの影響を調べた。二プロセスで作製した試料の曲げ強さと破壊靭性は低温で改善することを見ることができる。応力誘起マルテンサイト変態強靭化機構をその場Raman法により確認した。正方晶ZrO_2は温度が298Kから77Kに低下したときに発生する残留応力のために変換するより容易であると考えられる。,変態強靭化効果が強くなる,機械的性質の増加をもたらすであろう。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 焼結 ,  曲げ強さ ,  正方晶系 ,  破壊靱性 ,  *極低温 ,  残留応力 ,  機械的性質 ,  *低温 ,  *セラミック
準シソーラス用語： 加工誘起マルテンサイト ,  焼結温度 ,  *強靱化 , 【Automatic Indexing@JST】