MG-GD-Y-ZN-MN合金のLPSO相とその微細構造に及ぼす圧延工程の影響を研究した。【JST・京大機械翻訳】

Influences of rolling processes on LPSO phase, microstructure and property of Mg-Gd-Y-Zn-Mn alloy

著者 (6件)： Wang Jingfeng (National Engineering Research Center for Magnesium Alloys, Chongqing University, The State Key Laboratory of Mechanical Transmission) ,  Huang Xiuhong (National Engineering Research Center for Magnesium Alloys, Chongqing University) ,  Xie Feizhou (National Engineering Research Center for Magnesium Alloys, Chongqing University) ,  Huang Song (National Engineering Research Center for Magnesium Alloys, Chongqing University) ,  Hou Fan (National Engineering Research Center for Magnesium Alloys, Chongqing University) ,  Pan Fusheng (National Engineering Research Center for Magnesium Alloys, Chongqing University)
資料名： Zhongguo Youse Jinshu Xuebao  (Zhongguo Youse Jinshu Xuebao)
巻： 26  号： 8  ページ： 1588-1596  発行年： 2016年 
JST資料番号： W0943A  ISSN： 1004-0609  CODEN： ZYJXFK  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： MG-GD-Y-ZN-MN合金中のLPSO相とその微細構造に及ぼす「圧延+溶体化+圧延」と「溶体化+圧延」の影響を研究した。結果は以下を示す。「圧延+溶体化+圧延」プロセスで処理した後、合金中の塊状LPSOは小さく、しかも分布が分散し、合金のミクロ組織は微細な再結晶粒からなり、最終合金は良好な総合機械的性質を得て、引張強度(UTS)は347MPAに達した。伸び率(EL)は11.6%であった。「溶体化+圧延」プロセスで処理した後、合金中の塊状LPSOは粗大、分布不均一であり、固溶化焼鈍後析出した層状LPSO相は合金の再結晶を阻害するため、圧延後合金中に変形組織が存在する。最終的に,合金は比較的高い引張強さ(UTSMPA)を示したが,伸び率は低かった(EL=6.6%)。対照的に,「圧延+溶体化+圧延」プロセスは,より大きな機械的性質を得るために,より大きな圧延を行い,そして,より高い機械的性質を得ることができた。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 伸び率 ,  結晶粒 ,  焼なまし ,  微細構造 ,  機械的性質 ,  再結晶 ,  *圧延 ,  引張強さ ,  *合金 ,  変形組織 ,  溶体化処理
準シソーラス用語： *LPSO相 , 【Automatic Indexing@JST】

著者キーワード (5件)： Mg-Gd-Y-Zn-Mn alloy ,  rolling process ,  LPSO phase ,  microstructure ,  mechanical property

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (4件)： LPSO相 ,  微細構造 ,  圧延工程 ,  研究