RTMプロセス用ビニルエステル樹脂系の硬化動力学【JST・京大機械翻訳】

Application in RTM of the vinyl ester resin curing kinetics

著者 (8件)： Zhao Xiaolin (School of Materials Science and Engineering,University of Science and Technology Beijing) ,  Du Jianhua (Department of Science Research,Academy of Armored Force Engineering) ,  Gao Heng (Department of Self-propelled Gun,Nanjing Artillery Academy) ,  Fan Tao (School of Materials Science and Engineering,University of Science and Technology Beijing) ,  Li Hui (Department of Science Research,Academy of Armored Force Engineering) ,  Wang Dafeng (School of Materials Science and Engineering,University of Science and Technology Beijing) ,  Lv Yingying (School of Materials Science and Engineering,University of Science and Technology Beijing) ,  Jia Chengchang (School of Materials Science and Engineering,University of Science and Technology Beijing)
資料名： Fenmo Yejin Jishu  (Fenmo Yejin Jishu)
巻： 34  号： 5  ページ： 336-340  発行年： 2016年 
JST資料番号： C2397A  ISSN： 1001-3784  CODEN： FYJIEQ  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 示差走査熱量測定(DSC)を用いて,樹脂A-ビニル樹脂系の硬化プロセスを研究し,硬化系のDSC曲線に及ぼす加熱速度の影響を分析した。そして,KISSINGER方程式とCRANE方程式を用いて,硬化速度論方程式を確立した。この反応系の反応動力学方程式は,T=1-[1-5 65EXP(-4352.90/T)T](6)であった。温度-加熱速度(T-Β)外挿法を用いて,ゲル化温度,硬化温度,硬化温度などの硬化プロセスパラメータを理論的に得た。66,74。55,95。49°C。実際の応用では,内部熱反応が存在するため,使用温度を適切に低下させる。硬化動力学方程式と硬化プロセスパラメータは,樹脂移動成形(RTM)プロセスに重要な役割を果たす。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 反応系 ,  示差走査熱量測定 ,  *運動論的方程式 ,  プロセスパラメータ ,  加熱速度 ,  外挿法 ,  熱化学反応 ,  速度論 ,  ゲル化
準シソーラス用語： 硬化温度 , 【Automatic Indexing@JST】

著者キーワード (3件)： Vinyl ester resin ,  DSC ,  Cure kinetics

分類 (2件)： 高分子と低分子との反応  (CG03020L) ,  橋かけ  (YH04100E)

タイトルに関連する用語 (5件)： RTM ,  プロセス ,  ビニルエステル樹脂 ,  硬化 ,  動力学