U-MO合金とZR-4合金の拡散層性質の研究【JST・京大機械翻訳】

Study on Characterization of Diffusion Layer Between U-Mo Alloy and Zr-4 Alloy

著者 (7件)： Chen Jiangang (Key Laboratory of Nuclear Reactor Fuel and Materials, Nuclear Power Institute of China) ,  Yin Changgeng (Key Laboratory of Nuclear Reactor Fuel and Materials, Nuclear Power Institute of China) ,  Liu Yunming (Key Laboratory of Nuclear Reactor Fuel and Materials, Nuclear Power Institute of China) ,  Sun Changlong (Key Laboratory of Nuclear Reactor Fuel and Materials, Nuclear Power Institute of China) ,  Li Chuanfeng (Key Laboratory of Nuclear Reactor Fuel and Materials, Nuclear Power Institute of China) ,  Liu Lijian (Key Laboratory of Nuclear Reactor Fuel and Materials, Nuclear Power Institute of China) ,  Du Peinan (Key Laboratory of Nuclear Reactor Fuel and Materials, Nuclear Power Institute of China)
資料名： He Kexue yu Gongcheng  (He Kexue yu Gongcheng)
巻： 36  号： 6  ページ： 771-775  発行年： 2016年 
JST資料番号： C2033A  ISSN： 0258-0918  CODEN： HYGODG  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 本論文では,U-MO合金とZR-4合金の拡散層特性を研究した。3つのサンドイッチ構造のU-MO/ZR-4拡散は,760~800°Cでの熱間圧延後,10~66時間保持した。拡散層の形態と厚さを走査型電子顕微鏡(SEM)によって分析し,拡散層における元素の分布を共鳴(WDS)によって分析し,拡散層の相組成をX線回折(XRD)にその結果,800°Cの高温でさえも,U-MO/ZR-4の拡散度は弱く,良好な相溶性を示した。U-MO/ZRの拡散層の中間層には亀裂があり、き裂の両側の拡散層の組成は明らかに異なり、U-MO側にはMOリッチ相があり、それは主に化合物ZRMO_2をベースとZR-4側のZRリッチ相は,化合物UZR_2をベースとする固溶体であった。クラックはUとZRの不等原子の交換によるものと考えられる。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 高温 ,  *拡散層 ,  固溶体 ,  共鳴 ,  相溶性 ,  サンドイッチ構造 ,  相組成 ,  熱間圧延 ,  X線回折 ,  *合金 ,  亀裂 ,  走査電子顕微鏡
準シソーラス用語： 中間層 , 【Automatic Indexing@JST】

著者キーワード (3件)： U-Mo alloy ,  Zr-4 alloy ,  Diffusion layer