アルブミン含有環境におけるCoCrMo合金の表面下微細組織発達に及ぼす電気化学的腐食の影響【Powered by NICT】

Effect of electrochemical corrosion on the subsurface microstructure evolution of a CoCrMo alloy in albumin containing environment

著者 (4件)： Wang Zhongwei (Corrosion and Protection Center, Key Laboratory for Environmental Fracture (MOE), University of Science and Technology Beijing, 100083, China) ,  Yan Yu (Corrosion and Protection Center, Key Laboratory for Environmental Fracture (MOE), University of Science and Technology Beijing, 100083, China) ,  Su Yanjing (Corrosion and Protection Center, Key Laboratory for Environmental Fracture (MOE), University of Science and Technology Beijing, 100083, China) ,  Qiao Lijie (Corrosion and Protection Center, Key Laboratory for Environmental Fracture (MOE), University of Science and Technology Beijing, 100083, China)
資料名： Applied Surface Science  (Applied Surface Science)
巻： 406  ページ： 319-329  発行年： 2017年 
JST資料番号： B0707B  ISSN： 0169-4332  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 金属インプラントの表面下微細構造は,トライボ腐食に重要な役割を果たす。局所環境の摩耗や変化のため,インプラント表面は不均一な電気化学的腐食特性を持つことができる。本研究では,人工関節のためのCoCrMo合金の表層下微細構造の進展に及ぼす電気化学的腐食条件の影響を調べた。透過型電子顕微鏡(TEM)を用いて,シミュレートされた生理学的溶液中で種々の印加電位で摩耗領域の表面下微細構造を観察した。結果は印加電位は表面不動態化を変えることなく合金表面上への蛋白質の吸着に影響を与えるのみならず表面下変形の重症度に影響を及ぼすことを示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 摩耗 ,  *腐食 ,  生理学 ,  *アルブミン ,  人工関節 ,  電位 ,  *微細構造 ,  *合金 ,  表層 ,  タンパク質 ,  透過型電子顕微鏡
準シソーラス用語： 重症度 ,  表面不動態化 ,  印加電圧 ,  *電気化学的腐食 , 【Automatic Indexing@JST】

著者キーワード (6件)： コバルト ,  バイオトライボ腐食 ,  AES ,  EIS ,  TEM ,  Interfaces

分類 (3件)： 電極過程  (CB07040U) ,  防食  (WB03040M) ,  腐食  (WB03030B)

タイトルに関連する用語 (5件)： アルブミン ,  環境 ,  微細組織 ,  発達 ,  電気化学的腐食