広い温度範囲におけるバランスのとれた強度と延性を有する直接鋳造バルク共晶および共晶に近い高エントロピー合金【Powered by NICT】

Directly cast bulk eutectic and near-eutectic high entropy alloys with balanced strength and ductility in a wide temperature range

著者 (13件)： Lu Yiping (Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China) ,  Gao Xuzhou (School of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094, PR China) ,  Jiang Li (Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China) ,  Chen Zongning (Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China) ,  Wang Tongmin (Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China) ,  Jie Jinchuan (Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China) ,  Kang Huijun (Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China) ,  Zhang Yubo (Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China) ,  Guo Sheng (Surface and Microstructure Engineering Group, Materials and Manufacturing Technology, Chalmers University of Technology, SE-41296 Gothenburg, Sweden) ,  Ruan Haihui (Department of Mechanical Engineering, The Hong Kong Polytechnic University, Hung Hom, Hong Kong, China) ,  Zhao Yonghao (School of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094, PR China) ,  Cao Zhiqiang (Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China) ,  Li Tingju (Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China)
資料名： Acta Materialia  (Acta Materialia)
巻： 124  ページ： 143-150  発行年： 2017年 
JST資料番号： A0316A  ISSN： 1359-6454  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 高エントロピー合金(HEA)は,通常,弱い流動性と鋳造性,およびかなりの組成不均一性を持ち,主としてそれらが高濃度で,多数の要素を含んでいるからである。結果として,鋳造によるHEAの大規模生産は限られている。問題に対処するために,共晶高エントロピー合金(EHEAs)の概念を提案した,これは良好な品質工業規模HEAインゴットを達成するために有望につながっていると,さらに重要なことに,良好な機械的性質。実用的大規模鋳造では,設計したEHEAsの実際の組成は共晶組成からずれる可能性がある。EHEAsの機械的性質に及ぼすこのような偏差の影響は,工業生産,本研究の主題を構成するために重要である。ここでは,共晶組成:亜共晶合金,共晶合金と過共晶合金に近い工業規模HEAインゴットを作製した。著者らの結果は,共晶組成からのずれは機械的性質,鋳造性に著しい影響を及ぼさず,EHEAsの良好な機械的性質を広い組成範囲で,室温と超低温で達成できることを示した。著者らの結果は,同時高強度と高延性を持つEHEAs,良好な流動性と鋳造性を大規模工業生産にすぐに適用できることを示唆した。共晶及び準共晶HEAの変形挙動とミクロ組織進展を技術の組み合わせ,ディジタル画像相関,その場シンクロトロンX線回折,および透過型電子顕微鏡による歪測定を用いて研究した。EHEAsにおけるネッキングの波状歪分布,生じる遅延を初めて報告した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 透過型電子顕微鏡 ,  過共晶合金 ,  *延性 ,  X線回折 ,  流動性 ,  歪測定 ,  *鋳造 ,  亜共晶合金 ,  鋳造性 ,  歪分布 ,  インゴット ,  *共晶 ,  共晶合金 ,  不均一性
準シソーラス用語： *高エントロピー合金 , 【Automatic Indexing@JST】

著者キーワード (5件)： 高エントロピー合金 ,  工業規模鋳造 ,  機械的性質 ,  共晶 ,  その場X線回折

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (7件)： 温度範囲 ,  バランス ,  延性 ,  鋳造 ,  バルク ,  共晶 ,  高エントロピー合金