SO_4(2-)は,X100パイプライン用鋼における孔食塩漬性溶液挙動の影響を及ぼしていた。【JST・京大機械翻訳】

Effects of SO_4(2-) on pitting corrosion behavior of X100 pipeline steel in alkaline solution

著者 (7件)： Shi Zhiqiang (College of Mechanical & Electronic Engineering in China University of Petroleum(Qingdao)) ,  Zhang Xiuyun (Guangxi Gas Pipeline Company Limited) ,  Wang Yanfang (College of Mechanical & Electronic Engineering in China University of Petroleum(Qingdao)) ,  Liu Mingxing (College of Mechanical & Electronic Engineering in China University of Petroleum(Qingdao)) ,  Tang Kang (College of Mechanical & Electronic Engineering in China University of Petroleum(Qingdao)) ,  Si Shuangshuang (College of Mechanical & Electronic Engineering in China University of Petroleum(Qingdao)) ,  Li Hao (College of Mechanical & Electronic Engineering in China University of Petroleum(Qingdao))
資料名： Zhongguo Shiyou Daxue Xuebao. Ziran Kexue Ban  (Zhongguo Shiyou Daxue Xuebao. Ziran Kexue Ban)
巻： 40  号： 1  ページ： 128-133  発行年： 2016年 
JST資料番号： W0621A  ISSN： 1673-5005  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 異なる質量分率のSO_4(2-)の塩漬性土壌シミュレーション溶液中の電気化学的試験技術の研究をX100パイプライン用鋼の孔食挙動により,そして走査振動電極技術(SVET)をその腐食機構を分析し,腐食モデルを確立した。結果:試料は,異なる質量分率SO_4(2-)の土壌の模擬溶液においていずれも表現の典型的活性溶解である;SO_4(2-)質量分率は増加し,分極抵抗は著しい増加に伴い,自己腐食電流密度は低下し,X100パイプライン用鋼の孔食の傾向は減少し,SO_4(2-),KU’ERLE土壌中で腐食抑制アニオンに属する発生説明された。その腐食メカニズムはエッチピットの表面には,SO_4(2-)とCL-はCL-を競争的に吸着作用が優先吸着によって抑制したX100パイプライン用鋼の腐食では主に,同時に生成するFES腐食生成物膜は腐食孔表面を覆い,腐食速度が低下した。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： エッチピット ,  腐食機構 ,  電流密度 ,  吸着 ,  腐食 ,  *パイプライン用鋼 ,  腐食抑制作用 ,  電気化学 ,  腐食生成物 ,  溶解 ,  *塩漬 ,  アニオン ,  腐食速度 ,  分極抵抗
準シソーラス用語： 質量分率 , 【Automatic Indexing@JST】

著者キーワード (5件)： X100 pipeline steel ,  alkaline solution ,  SO_4(2-) ,  Cl- ,  pitting corrosion

分類 (3件)： 腐食  (WB03030B) ,  電極過程  (CB07040U) ,  腐食基礎理論,腐食試験  (WB03020Q)

タイトルに関連する用語 (5件)： パイプライン用鋼 ,  孔食 ,  塩漬 ,  溶液 ,  挙動